PLASTIK KOMPOSIT KITOSAN-TiO2 NANOTUBE COMPOSITE PLASTIC OF CHITOSAN-TiO2 NANOTUBES

widya primanti, Dr. Indriana Kartini, M.Si

2012 | Tesis | S2 Ilmu Kimia

Karakterisasi Telah dilakukan preparasi plastik kitosan dengan berbagai konsentrasi kitosan dan plastik komposit kitosan-TiO2 nanotube menggunakan metode cetak. Plastik komposit diharapkan mempunyai sifat ketahanan terhadap paparan radiasi UV lebih baik daripada plastik kitosan. terhadap plastik yang dihasilkan dilakukan menggunakan universal testing machine, spektrofotometer UV-Vis, FTIR dan XRD. Pengujian ketahanan plastik terhadap radiasi UV dilakukan menggunakan lampu UV (λ = 254 nm) selama 72 jam. Perubahan sifat plastik dikaji melalui analisis plastik menggunakan spektrofotometer FTIR, XRD dan spektrofotometer UV-Vis. Spektrofotometer UV-Vis digunakan untuk mengkaji sensitivitas absorpsi plastik di daerah panjang gelombang UV dan opasitas plastik. Semua plastik kitosan dan plastik komposit kitosan-TiO2 nanotube mengalami peningkatan absorbansi pada panjang gelombang 260-340 nm akibat paparan radiasi UV selama 72 jam. Plastik kitosan dengan penambahan TiO2 nanotube menunjukkan perubahan absorbansi yang lebih kecil daripada plastik kitosan. Plastik komposit kitosan TiO2 nanotube dengan konsentrasi TiO2 nanotube 0,05% (b/v) menunjukkan perubahan absorbansi dan opasitas yang paling kecil.

Study of preparation of chitosan and chitosan-TiO2 composite plastic at various chitosan concentration by solvent casting technique has been done. The composite plastics are expected to have higher UV radiation barrier properties than the chitosan plastic. The resulted plastics were characterized by Universal testing machine, FTIR, UV-Vis spectrophotometers and XRD. The UV-light barrier properties of the resulted plastics were tested by radiating the plastics under UV-light (λ = 254 nm) for 72 hours. The radiated plastics were then analyzed by FTIR, UV-Vis spectrophotometers and XRD. It is found that all chitosan-based plastics showed increasing absorbance at wavelength of 260-340 nm after UV-light radiation for 72h. The parent chitosan plastics were more susceptible to UV irradiation than the composite plastics of chitosan-TiO2 nanotube. Composite plastic of chitosan-TiO2 nanotube 0.05% (w/v) has shown the highest UV barrier properties.

Kata Kunci : kitosan, TiO2 nanotube, plastik kitosan, plastik komposit kitosan TiO2 nanotube.