PENGARUH SUHU CETAKAN, PENGHALUS BUTIR ALTiB DAN KECEPATAN PUTAR TERHADAP SIFAT FISIS DAN MEKANIK PRODUK PENGECORAN ALUMINIUM SCRAP

Nugroho Santoso, ST, Dr. Eng. Priyo Tri Iswanto, ST, M. Eng.

2011 | Tesis | S2 Teknik Mesin

Aluminium bekas adalah bahan baku coran yang sering digunakan pada industri coran di wilayah Yogyakarta untuk memproduksi berbagai macam peralatan rumah tangga dan komponen kendaraan. Permasalahan yang sering dihadapi pengrajin coran aluminium yang menggunakan cetakan logam adalah sering terjadinya cacat coran dan kualitas coran yang kurang baik. Peneliti menganalisa pengaruh gaya sentrifugal pada pengecoran metode centrifugal casting mencegahan cacat coran dan meningkatan kualitas material hasil coran.Tahapan proses penelitian adalah memotong material, melebur pada temperatur 750 o C, memanaskan cetakan, penambahan inokulan Al TiB pada cairan logam, pengaturan putaran cetakan 0, 280, 700 rpm, penuangan, pembongkaran hasil coran, pemeriksaan coran, analisa kekuatan coran dengan uji tarik, kekerasan, impak dan analisa struktur mikro.Dari hasil pengamatan dan analisa pengujian diketahui bahwa pada temperatur cetakan 200 o C sampai 350 o C terjadi penurunan kekerasannya 71,67 VHN sampai 56,83 VHN, penambahan Al TiB 0,08 % sampai 0,8 % terjadi penurunan kekerasannya 76,58 BHN sampai 58,45 BHN dan penurunan kekuatan tariknya dari 176,2 MPa sampai 101,7 MPa. Putaran cetakan 0, 280, 700 rpm dapat mencegah cacat penyusutan luar dan peningkatan kekuatan mekanik yaitu nilai kekerasannya ( 31,52, 34,72, 37,15 ) BHN, nilai kekuatan tariknya ( 148,87, 169,36, 176,89 ) MPa, nilai impak (0,028, 0,026, 0,063) J/mm 2 .

Scrap aluminum is a raw material often used in industrial castings in Yogyakarta to produce a variety of housewares and auto parts. Problems often encountered by the craftsmen are, among others, aluminum casting using a metal casting mold casting produces defects and low quality of the casting products. The researcher analyzed the influence of the centrifugal force on centrifugal casting method aimed at preventing defects of the casting products and improving the quality of the casting products. The stages of the research are first, cutting the material; second, melting it at the 750oC, heating the mold, adding the Al TIB inoculant to the metal liquid, setting the mold rotation at 0, 280, 700 rpm then pouring the casting material into the casting mold. After that picking up the products of castings, inspecting casting products, analyzing the strength of the casting products with a tensile test, hardness and impact tests, and finally analyzing the microstructures of the casting products. From the observation and the analysis of the casting experiment and tests, it is found that the hardness of the casting products decreases at the mold temperature of 200oC to 350oC from 71.67 VHN to 56.83 VHN, the addition of 0.08 % to 0.8 % of Al TiB inoculants decreases the hardness of the products from 76.58 BHN to 58.45 BHN and its pulling strength decreases from 176.2 MPa to 101.7 MPa. The mold rotation at 0, 280, 700 rpm prevents the product from external shrinkage defects and increases the mechanical strength of the hardness at 31.52, 34.72, 37.15 BHN the pulling strength of the products at 148.87, 169.36, 176.86 MPa, and the impact value at ( 0.028, 0.026, 0.063) J/mm2.

Kata Kunci : Gaya sentrifugal, Pengecoran sentrifugal.