OPTIMASI SISTEM PEMBUATAN PAPAN PARTIKEL DARI SERABUT BUAH PINANG

Budi Istana, Dr. Ing. Ir. Kusnanto

2011 | Tesis | S2 Mag.Sistem Teknik

Penelitian ini bertujuan untuk mengetahui sifat fisik dan mekanik serta nilai absorbsi papan partikel dengan menggunakan metode tabung impedansi. Papan partikel dalam pengujian ini dibuat dari l i m b ah serabut buah pinang dengan bahan jenis perekat yang digunakan adalah perekat komersial urea formaldehida (UF) dengan kadar perekat divariasikan 10% dan 15% berdasarkan berat kering tanur dengan target kerapatan 0,4 g/cm3; 0,6 g/cm3; 0,9 g/cm3 dan dikempa dengan mesin kempa panas dengan tekanan 200 bar dengan suhu 130oC selama 10 menit. Untuk pengujian kuat lentur dan uji tarik tegak lurus permukaan diuji menggunakan alat Universal Wood Testing Machine (UWTM) di Laboratorium mekanika Bahan Universitas Gadjah Mada. Sedangkan untuk pengujian absorbsi menggunakan tabung impedansi di Laboratorium Getaran Akustik Fakultas Teknik Mesin Universitas Gadjah Mada. Data hasil pengujian dianalisis dengan perhitungan MOE dan MOR.berturut Hasil yang diperoleh dalam pengujian menunjukkan nilai rata-rata kerapatan papan yang dihasilkan -turut adalah 0,402 g/cm3, 0,601 g/cm3 dan 0,922 g/cm3 untuk papan berkadar perekat 10% sedangkan untuk perekat 15% ratarata kerapatan papan yang dihasilkan adalah 0,406 g/cm3, 0,618 g/cm3, 0,955/cm3. MOE untuk spesimen dengan kadar perekat 10% sebesar 2302,59 kg/cm2; 5412,74kg/cm2; 7996,63 kg/cm2 dan untuk perekat 15% sebesar 2752,89 kg/cm2; 5457,53kg/cm2; 9306,14 kg/cm2. Nilai rata-rata nilai MOR untuk spesimen dengan kadar perekat 10% sebesar 47,83 kg/cm2; 124,97 kg/cm2; 304,69 kg/cm2 dan untuk spesimen dengan kadar perekat 15% sebesar 67,24 kg/cm2; 154,99 kg/cm2; 307,06 kg/cm2. Nilai rata-rata kuat tarik tegak lurus permukaan untuk spesimen dengan kadar perekat 10% sebesar 3,17 kg/cm2; 9,49 kg/cm2; 14,91 kg/cm2 dan untuk spesimen dengan kadar perekat 15% sebesar 4,56 kg/cm2; 10,17 kg/cm2; 18,37 kg/ cm2. Ditinjau dari papan partikel yang dihasilkan termasuk dalam kategori papan partikel berkualitas menengah. Untuk pengujian absorbsi papan partikel yang dihasilkan pada frekuensi 500 Hz sebagai reratanya sebesar 0,9 sehingga termasuk kategori papan partikel berkualitas tinggi dengan klasifikasi A dalam standart ISO 11654.

The study aimed at investigating the physical and mechanical properties and the absorption value of particle board using impedance tube method. The particle board in the test was made of areca fiber waste and comercial addhesive urea formaldehyde (UF) with the variations of 10% and 15% based on oven dried weight with the density targets of 0.4 g/cm3, 0.6 g/cm3, 0.9 g/cm3 and were pressed at 200 bar, with Temp 130oC for 10 minutes. The flexibility strength and surface perpendicular pulling tests were conducted using Universal Wood Testing Machine (UWTM) in the Mechanics Laboratory of Gadjah Mada University. Meanwhile, the absorption test was conducted using impedance tube in the Accoustic Vibration Laboratory of the Faculty of Machine Engineering of Gadjah Mada University. The data resulting from the tests was analyzed by caltulating MOE and MOR. The results of the study showed that the average density values of the resulting board were 0.402 g/cm3, 0.601 g/cm3and 0.922 g/cm3 for the board with the adhesive content of 10%, while the average density values of the board with the adhesive content of 1% were 0.406 g/cm3, 0.618 g/cm3 and 0.955 g/cm3. The MOEs for the specimen with the adhesive content of 10% was 2302.59 kg/cm2, 5412.74 kg/cm2, 7996.63 kg/cm2 and the MOEs with the adhesive content of 15% were 2752.89 kg/cm2 , 5457.53 kg/cm2 and 9306.14 kg/cm2. The average values of the MOR for the specimen with the adhesive content of 10% were 47.83 kg/cm2, 124.97 kg/cm2, 04.69 kg/cm2 and for the specimen with the adhesive content of 15% were 67.24 kg/cm2 , 154.99 kg/cm2 and 307.06 kg/cm2. The average values of the surfaceperpendicular pulling test of the specimen with the adhesive content of 10% were 3.17 kg/cm2, 9.49 kg/cm2 and 14.91 kg/cm2 and for the specimen with the adhesive content of 15% were 4.56 kg/cm2, 10.17 kg/cm2 and 18.37 kg/cm2. Concerning with the resulting board, the board was classified to medium quality board. The particle board absorption test at the frequency of 500 Hz gave the average value of 0.9 and it was categorized into high quality particle board with the classification A in ISO 11654 standard.

Kata Kunci : serabut buah pinang, Papan partikel, Sifat mekanika, Absorbsi.