SINTESIS KOMPOSIT Fe-TiO2-SiO2 SEBAGAI FOTOKATALIS PADA DEGRADASI ERIONYL YELLOW

DEVI INDAH ANWAR, Prof. Dr. Bambang Rusdiarso, DEA.

2011 | Tesis | S2 Ilmu Kimia

Pada penelitian ini telah dilakukan sintesis dan karakterisasi komposit Fe-TiO2-SiO2 sebagai fotokatalis pada fotodegradasi zat warna erionyl yellow, pada paparan sinar ultraviolet dan sinar tampak dalam reaktor tertutup. Sintesis komposit dilakukan dengan metode sol-gel pada temperatur kamar menggunakan tetraetilortosilikat (TEOS), titanium tetraisopropoksida (TTiP) dan besi (III) klorida sebagai prekursor, yang dilanjutkan dengan perlakuan termal pada temperatur 500oC. Karakterisasi dilakukan dengan metode difraksi sinar-X, spektrometri infra merah, spektrofotometri difusi reflektansi UV-Vis dan fluoresensi sinar-X. Pada uji ini telah dipelajari pengaruh pH awal larutan, konsentrasi ion logam besi (III), dan waktu penyinaran terhadap efektivitas fotodegradasi erionyl yellow. Hasil penelitian menunjukkan bahwa komposit Fe-TiO2-SiO2 dapat disintesis dengan metode sol-gel pada temperatur kamar, diikuti perlakuan termal dengan konsentrasi optimum ion besi (III) 6% berat. Komposit Fe-TiO2-SiO2 meningkatkan efektivitas fotodegradasi erionyl yellow secara signifikan pada kondisi pH 2 dan waktu pemaparan 16 jam, dengan hasil persentase degradasi sebesar 57,87% pada paparan sinar ultraviolet dan 95,11% pada paparan sinar tampak.

Synthesis and characterization of Fe-TiO2-SiO2 composite as a photocatalyst in the photodegradation of erionyl yellow on ultraviolet and visible light irradiation in a closed reactor have been carried out. Synthesis was conducted by the sol-gel method at room temperature using tetraethylorthosilicate (TEOS), titanium tetraisopropoxide (TTiP) and iron (II) chloride as a precursor, followed by thermal treatment at a temperature of 500oC. The characterizations were performed using X-ray diffraction (XRD), FT-IR spectrometry, UV-Vis diffuse reflectance spectrofotometry and fluorescence X-rays. In the activity test, the influence of initial pH, metal ion concentration of iron, and time of irradiation on the effectiveness of photodegradation erionyl yellow have been investigated. The results showed that the Fe-TiO2-SiO2 composite could be synthesized by sol-gel method at room temperature, followed by thermal treatment with the optimum concentration of iron was 6% weight. Fe-TiO2-SiO2 composite increase the effectiveness of photodegradation erionyl yellow significantly at pH 2 and irradiation time of 16 hours, with the percentage degradation of 57.87% and 95.11% for under ultraviolet and visible light irradiation, respectively.

Kata Kunci : komposit Fe-TiO2-SiO2, fotokatalis, fotodegradasi, erionyl yellow