ADSORPSI Fe(III) DAN Cd(II) PADA POLIEUGENOL TERSAMBUNG SILANG BISFENOL A DIGLISIDIL ETER

WIDYA SARTIKA SULISTIANI, Dr. Dwi Siswanta, M.Eng.

2011 | Tesis | S2 Ilmu Kimia

Telah dilakukan studi adsorpsi Fe(III) dan Cd(II) pada polieugenol tersambung silang bisfenol A diglisidil eter (BADGE). Reaksi sambung silang polieugenol dengan BADGE dilakukan dalam suasana basa dan direfluks selama 6 jam. Padatan hasil sintesis dikarakterisasi dengan Spektrofotometri Fourier- Transform Infrared (FTIR) dan Scanning electron microscope (SEM). Proses adsorpsi Fe(III) dan Cd(II) dilakukan dalam sistem batch dengan variabel pH, waktu kontak, dan konsentrasi ion logam. Selektivitas adsorpsi Fe(III) dipelajari dengan adsorpsi kompetitif terhadap ion Cd(II). Pengaruh modifikasi terhadap proses adsorpsi Fe(III) dan Cd(II) dipelajari dengan membandingkan adsorpsi pada polieugenol dan polieugenol-BADGE. Analisis konsentrasi Fe(III) dan Cd(II) sebelum dan sesudah adsorpsi dilakukan dengan menggunakan spektrometer serapan atom (SSA). Karakterisasi polieugenol-BADGE dengan FTIR menunjukkan hilangnya serapan tekukan OH dalam bidang pada 1365,60 cm-1 dan munculnya serapan tajam aromatik tersubstitusi pada 825,53 cm-1. Adsorpsi optimum Fe(III) dan Cd(II) pada kedua adsorben terjadi pada pH 4 dan pH 5 dengan mengikuti model kinetika orde pseudo-2. Konstanta laju adsorpsi Fe(III) pada polieugenol dan polieugenol-BADGE pada pH optimum berturut-turut 0,039 dan 0,047 g g-1 min-1 dengan kapasitas adsorpsi berdasarkan model isotermal Langmuir masing-masing adalah 166,67 dan 200 mg/g. Konstanta laju adsorpsi Cd(II) pada pH optimum untuk adsorben polieugenol dan polieugenol-BADGE berturut turut adalah 0,61 dan 3,08 g g-1 min-1 dan kapasitas adsorpsinya adalah 0,035 mg/g untuk polieugenol dan 0,041 mg/g untuk polieugenol-BADGE. Modifikasi polieugenol dapat meningkatkan kapasitas adsorpsi dan selektivitas adsorpsi Fe(III) terhadap adanya Cd(II).

A study of adsorption of Fe (III) and Cd (II) on bisphenol A diglycidyl ether (BADGE)-crosslinked polyeugenol has been conducted. Crosslinking reaction of polieugenol with BADGE was conducted under alkaline conditions and refluxed for 6 hours. The products were characterized by spectroscopy Fourier-Transform Infrared (FTIR) and Scanning electron microscope (SEM). The adsorption of Fe (III) and Cd (II) were conducted by the batch method with variable pH, contact time, and concentration of adsorbate. Selectivity of adsorption of Fe (III) was studied by competitive adsorption against Cd(II). Effect of the polyeugenol modifications to the adsorption of Fe (III) and Cd II) was studied by comparing the adsorption on polyeugenol and BADGE-crosslinked polyeugenol. The concentration of Fe(III) and Cd(II) before and after adsorption were determined using atomic absorption spectrophotometer (AAS). Characterization of BADGE-crosslinked polyeugenol by FTIR showed the disappearance of OH bending absorption at 1365.60 cm-1 and the presence of a sharp absorption of substituted aromatic at 825.53 cm-1. Optimum adsorption of Fe (III) and Cd (II) in the second adsorbent occurs at pH 4 and pH 5 by following the model of pseudo-second order kinetics. Adsorption rate constant of Fe (III) on polyeugenol and BADGE-crosslinked polyeugenol were 0.039 and 0.047 g g-1 min-1 successively with the adsorption capacity of each 166.67 and 200 mg/g. While the rate constant and adsorption capacity of Cd(II) on polieugenol at optimum pH were 0.61 g g-1 min-1 and 0.035 mg/g, and 3.08 g g-1 min-1 and 0.041 mg/g for BADGE-crosslinked polyeugenol respectively. Compared to unmodified polyeugenol, BADGE-crosslinked polyeugenol gave higher adsorption capacity and adsorption selectivity toward Fe(III) in the presence of Cd(II).

Kata Kunci : Adsorpsi, Polieugenol,Polieugenol-BADGE, Fe(III), Cd(II)