PEMANFAATAN PASIR LOKAL TARAKAN DAN BATU PECAH ASAL SEKATAK KABUPATEN BULUNGAN KALIMANTAN TIMUR SEBAGAI BAHAN PEMBUATAN BETON NORMAL

Arifay Saini, ST., Prof. Ir. Iman Satyarno, M.E., Ph.D.

2011 | Tesis | S2 Mag.Teknologi Bahan Bangn

Kota Tarakan merupakan satu pulau dalam Wilayah Kalimantan Timur Bagian Utara yang tidak mempunyai material bebatuan tapi mempunyai material pasir yg cukup banyak. Sehingga sampai saat ini material yang dipergunakan dalam setiap proses pembangunan sarana dan prasarana adalah material yang didatangkan dari luar yang secara ekonomis sangat mahal dan perlu waktu cukup lama dalam mobilisasi seperti material pasir dan batu pecah dari Palu, Toli-Toli, serta Tawau Malaysia Timur. Material agregat halus (pasir lokal Tarakan) dan agregat kasar (batu pecah) asal Sekatak Kabupaten Bulungan Kalimantan Timur belum pernah ada yg meneliti secara mendalam namun sudah ada yang memanfaatkannya sebagai bahan dasar pembuatan beton terutama beton non struktur. Penelitian ini bertujuan untuk mengetahui sifat dan karakteristik pasir lokal Tarakan dan batu pecah asal Sekatak sebagai bahan pembuat beton normal. Dalam penelitian ini bahan yang dipergunakan adalah pasir lokal Tarakan, batu pecah asal Sekatak Kabupaten Bulungan Kalimantan Timur, Semen Portland tipe I merk Tiga Roda dan air dari laboratorium Bahan Bangunan UGM. Rancangan adukan ditetapkan dengan nilai faktor air semen (fas) 0,4; 0,5; 0,6 dengan nilai slump 6±2 cm dan 10±2 cm. Tahap awal penelitian adalah melakukan pengujian sifat-sifat fisika dari pasir dan batu pecah, modulus halus butir, berat jenis SSD, berat satuan, kadar lumpur, daya serap air dan ketahanan aus yang mengacu pada SNI 03-6861.1-2002 (Spesifikasi Bahan Bangunan Bagian A, Bahan Bangunan Bukan Logam). Kemudian dilanjutkan dengan proses pembuatan benda uji yang bertujuan untuk mengetahui hubungan faktor air semen (fas) dan jumlah semen terhadap nilai slump dan kuat tekan beton. Hasil pemeriksaan menunjukkan pasir lokal Tarakan mempunyai nilai modulus halus butir (mhb) 1,612; berat jenis SSD 2,594 gr/cm³; berat satuan tanpa pemadatan 1,497 gr/cm³; daya serap air 1,110%; kandungan lumpur 1,328%. Sedangkan untuk batu pecah asal Sekatak Kabupaten Bulungan mempunyai modulus halus butir (mhb) 6,729; berat jenis SSD 2,504 gr/cm³; berat satuan tanpa pemadatan 1,431 gr/cm³; daya serap air 2,583%; dan kandungan lumpur 4,505%. Perbandingan agregat halus dan agregat kasar dalam penelitian ini adalah 30% : 70%. Beton fas 0,4 dengan kandungan semen berturut-turut 417,16 kg/m³ dan 455,90 kg/m³ mempunyai kuat tekan rata-rata 40,64 MPa dan 46,84 MPa, untuk fas 0,5 dengan kandungan semen berturut-turut 348,33 kg/m³ dan 374,90 kg/m³ mempunyai kuat tekan rata-rata 35,96 MPa dan 28,37 MPa, sedangkan untuk beton fas 0,6 dengan kandungan semen berturut-turut 285,34 kg/m³ dan 312,15 kg/m³ mempunyai kuat tekan rata-rata 26,52 MPa dan 24,53 MPa. Laju kenaikan kuat tekan beton pada umur 3,7 dan 28 hari adalah 61%, 80% dan 100%. Secara umum dapat disimpulkan bahwa pasir lokal Tarakan dan batu pecah asal Sekatak Kabupaten Bulungan Kalimantan Timur layak dijadikan bahan beton normal.

City of Tarakan is an island in the Northern Territory of East Kalimantan that has no material rocks but sand, which has quite a lot. So far the materials that are used in every process of building facilities and infrastructure is material brought in from outside who are economically very expensive and it took quite a while in the mobilization such as sand and crushed stone materials from Palu, Toli-Toli, as well as East Malaysia Tawau. Fine aggregate material (local sand Tarakan) and coarse aggregate (crushed stone) from East Kalimantan Sekatak Bulungan who has never been studied in depth but has some use in the manufacture of concrete, especially non-structural concrete. This study aims to determine the nature and characteristics of local sand and crushed stone from Tarakan Sekatak as material for normal concrete. In this research, the materials used are locally Tarakan sand, crushed stone Sekatak Bulungan origin East Kalimantan, Portland Cement Type I brand Tigaroda and water of Gadjah Mada University Building Materials laboratory. The design is set with mortar cement water cement ratio (wcr) 0,4; 0,5; 0,6 with the slump value 6±2 cm and 10±2 cm. The initial phase of the study is to test physical properties of sand and crushed stone, fine grain modulus, density SSD, weight unit, mud content, water absorption and wear resistance refers to the SNI 03-6861.1-2002 (Specification of Building Materials Section A, Non Metallic Building Materials). Then proceed with the process of making samples in order to determine the relationship between the water cement and the amount of cement to the slump value and strength of concrete. The assessment shows local sand Tarakan has fine grain modulus value 1,612; Saturated Surface Dry (SSD) specific gravity 2,594 gr/cm³; without compaction unit weight 1,497 gr/cm³; water absorption 1,110% and 1,328% mud content. As for the origin of crushed stone Sekatak Bulungan have fine grain modulus 6,729; Saturated Surface Dry (SSD) specific gravity 2,504 gr/cm³; without compaction unit weight 1,431 gr/cm³; water absorption 2,583% and 4,505% mud content. Comparison of fine aggregate and coarse aggregate in this study is 30%; 70%. Concrete containing cement for water cement ratio (wcr) 0,4 consecutive 417,16 kg/m³ and 455,90 kg/m³ has an average compressive strength of 40,64 MPa and 46,84 MPa, for water cement ratio (wcr) 0,5 with cement content of successive contributed 348,33 kg/m³ and 374,90 kg/m³ has an average compressive strength of 35,96 MPa and 28,37 MPa, whereas for concrete with cement content for water cement ratio (wcr) 0,6 consecutive 285,34 kg/m³ and 312,15 kg/m³ has an average compressive strength of 26,52 MPa and 24,53 MPa. The rate of increase in strength of concrete at age 3, 7 and 28 days is 61%, 80% and 100%. In general it can be concluded that the local sand and crushed stone from Tarakan Sekatak Bulungan East Kalimantan worthy of normal concrete material.

Kata Kunci : Pasir lokal Tarakan, batu pecah asal Sekatak Kabupaten Bulungan dan kuat tekan