PEMANFAATAN BATU PECAH BUKIT ROBAN DAN PASIR PUTIH KOTA SINGKAWANG UNTUK BAHAN PEMBUATAN BETON NORMAL

Hery Hermawan, ST., Prof. Ir. Iman Satyarno, M.E., Ph.D.

2011 | Tesis | S2 Mag.Teknologi Bahan Bangn

Berdasarkan Peraturan Walikota Singkawang nomor 44 tabun 2009 tentang lokasi dan jenis tambang galian c legal di Singkawang, ditetapkan untnk lokasi quarry pasir putih berada di belakang Dodiklat Singkawang Selatan seluas 36 hektar, dan quarry batu pecah berada di Jalan Barn (Bukit Roban) seluas 24 hektar. Sebagai tindak lanjut dari peraturan tersebut maka material pada quarry perlu diteliti untuk mengetahui sifat-sifat materialnya dan sifat beton normal dari materiallokal tersebut berupa kuat tekan, kuat lentur, modulus elastisitas clansifat kedap air pada beton. Bahan yang digunakan dalam penelitian ini adalah batu pecah bukit Roban, pasir putih kota Singkawang dan semen tipe PCC (Portland Composite Cement). Variasi perbandingan antara air dan semen (fas) adalah 0,4; 0,5 clan 0,6 dengan nilai slump 6:1::2em dan 10 x2 em. Uji kuat tekan beton dengan benda uji sHinderpada mnur 3,7 dan 28 hari. Uji serapan air dengan benda uji kubus clanuji kuat lentur balok dilakukan pada umur 28 hari. HasHpemeriksaan menunjukkan batu peeah bukit Roban mempunyai nilai modulus halus butir (mhb)- 7,62; berat jenis SSD 2,82; berat satuan tanpa pemadatan 1,59 gr/cm3; daya serap air 0,41%. Sedangkan untuk pasir putih kota Singkawang mempunyai modulus halus butir (mhb) 1,55; berat jenis SSD 2,59; bemt satuan tanpa pemadatan 1,44 gr/em);daya serap air 1,50%.Perbandingan aggregat halus dan aggregat kasar dalam penelitian ini adalah 32% pasir : 68% batu peeah. Beton dengan FAS 0,4 kandungan semen berturut-turut 431 kg/m) dan 470 kg/m3mempunyai kuat tekan rata-rata 39,49 MPa dan 33,26 MPa. Untuk FAS 0,5 kandungan semen berturut-turut 343 kg/m3 dan 375 kg/m3 mempunyai kuat tekan rata-rata 25,67 MPa dan 32,09 MPa. Untuk FAS 0,6 kandungan semen berturut-turut 285 kg/m3 dan 311 kg/m3 mempunyai kuat tekan rata-rata 25,11 MPa dan 22,26 MPa. Laju kenaikan kuat tekan beton pada umur 3,7 dan 28 hari berturut-turut 64, 81 clan 100%. Berdasarkan pengujian serapan air beton ini dinyatakan memenuhi standard beton kedap air nonnal (SNI 03-2914-1992). Moduluselastisitasbetonberkisarantara29019MPa- 33838MPadenganrumus modulus elastisitas beton E = 5800,7 .jt' c. Kandungan Ion khlorida (Cn pada beton berkisar antara 1,05% - 1,91% (terhadap berat semen) sehingga untuk mengatasi kandungan Ion khlorida (Cn yang besar tersebut campuran beton yang gibuat harus menggunakan jumlah semen minimal 500 kg/m3dengan fas 0,4 dan hanya terbatas untuk jenis beton bertulang yang selalu kering/terlindung dari lembab. ,

Based on Regulation of Mayor of Sir\gkawangNo 44, 2009 about location and type C of mine material in Singkawang, it is stated that location of white sand quarry is located behind of Dodildat Singkawang Selatan as 36 hectare, and for split quarry is located in Jalan Barn (Bukit Roban) as 24 hectare. As the follow up of this regulation, the quarry material needs to observe in order to know its material nature and nonnal concrete characteristic of those local materials, such as pressure force, flexible force, elasticity modulus and concrete waterproof. The material used in this research is split of Roban hill, white sand of Singkawang and PCC typed-cement (portland Composite Cement). The variation of water cement ratio (w/c) is 0,4; 0,5 and 0,6 by slump value of 6:1:2em and 10 :i:2em. The compression test of concrete by cilinder test material at the age of 3,7 and 28 days. Then, test of water absorption by cubic test material and bar flexible force test are conducted at 28 days. The examination result shows that split of Roban hill has soft grain modulus (mhb) value of 7,62; the specific weight of SSD is 2,82; unit weight without density is 1,59 gr/cm3; the water absorp power is 0,41%. Whereas, white sand of Singkawang has soft grain modulus (mhb) is 1,55; the specific weight of SSD is 2,59; unit weight without density is 1,44 gr/cm3; and the water absorp power is 1,50%. The comparison of soft and rough aggregate in the research is 32% of sand : 68% of split. Hence, concrete with w/c 0,4 of cement contain in respectively is 431 kg/m and 470 kg/m3 has average compression of 39,49 MPa and 33,26 MPa. For w/c 0,5 of cement contain in respectively is 343 kg/m3 and 375 kg/m3has average compression of 25,67 MPa and 32,09 MPa. For w/c 0,6 of cement contain in respectively is 285 kg/m3 and 311 kg/m3 has average compression of 25,11 MPa and 22,26 MPa. The rate of increasing compression of concrete at 3,7 and 28 days in respectively is 64, 81 and 100%. Based on the test of concrete water absorption, it is stated,that it meets the standard of concrete of nonnal waterproof (SNI 03-2914-1992). Concrete elasticity modulus ranges between 29019 MPa - 33838 MPa by formulation of concrete elasticity modulus E = 5800,7 .Jt'c. The contain of CWoride ion (Cn on the concrete ranges between 1,05% - 1,91% (upon cement's weight), so that to handle the bigger contain of Chloride ion (Cn of making concrete mixture should use the minimum amount of cement of 500 kg/m3with w/c 0,4 and only limits for type of reinforced concrete that is always dry Iprotected ITommoist.

Kata Kunci : batu pecah, pasir putih kota Singkawang, beton normal, kuat tekan