Sintesis komposit PVA-zeolit-clay dan uji adsorpsi-desorpsi terhadap campuran etanol-air

CIPTA, Indra, Dr. Yateman Arryanto

2010 | Tesis | S2 Ilmu Kimia

Sintesis komposit PVA-zeolit-clay dan uji adsorpsi – desorpsi terhadap campuran etanol air telah berhasil dilakukan. Komposit isintesis dengan mencampur zeolit-clay dalam rasio yang bervariasi ke dalam larutan PVA dengan konsentrasi yang bervariasi. Komposit kemudian dikarakterisasi dengan menggunakan spektroskopi inframerah dan difraktometer sinar –X untuk analisis struktur komposit, material testing machine untuk menguji kuat tekan (compressive strength). Uji adsorpsi – desorpsi etanol dan campuran etanol-air dilakukan dengan meneteskan sejumlah volume etanol pada bidang komposit dan mengamati lama waktu yang dibutuhkan komposit untuk menyerap sempurna, sedangkan uji desorpsi diukur berdasarkan pengurangan berat komposit per satuan waktu. Dengan meningkatnya konsentrasi PVA dan jumlah clay dalam komposit, meningkatkan kuat tekan komposit sampai lebih dari 3015,1 KPa dan mempercepat laju desorpsi etanol. Hasil kajian laju desorpsi menunjukkan laju desorpsi etanol jauh lebih cepat dibandingkan dengan laju desorpsi air. Perbedaan laju ini yang selanjutnya dijadikan dasar pemisahan campuran azeotrop etanol – air tanpa pemanasan. Hasil uji pendahuluan pervaporasi dengan menggunakan komposit , mengindikasikan komposit memiliki kemampuan untuk memisahkan campuran azeotrop etanol – air. Kata kunci: Pervaporasi, Komposit PVA-zeolit-clay

Polyvinyl alcohol (PVA) - zeolite - clay composite has been successfully prepared and used to investigate the adsorption-desorption rate of ethanol and ethanol- water mixtures. The composites were synthesized by stirring various weigth ratio of zeolite – clay in various weight of PVA solution. The composites are typically characterized by Fourier - Transformation Infrared (FTIR) spectroscopy and X-ray diffraction for determining the structure and material testing machine for measured the compressive strength of composites. The rate of adsorption - desorption was measuring by dropping ethanol in the composite and the observed the time for complete adsorption, and then the desorption rate was determined by observing the rate of weight reduction per minutes. Increasing amount of PVA and the amount of clay, increased the compressive strength of composite until more than 3015.1 KPa and accelerated the desorption rate of ethanol. Based on the desorption rate data showed the significant different between ethanol and water desorption. This desorption rate difference was then used as a reason to separate ethanol-water system through pervaporation method without heating treatment. From preliminary pervaporation, it was indicated that the composite had the ability to separate the azeotropic mixture of ethanol – water.

Kata Kunci : Pervaporasi,Komposit PVA,zeolit,clay,Adsorpsi,desorpsi,Etanol,air, Pervaporation, adsorption-desorption, ethanol-water