Kajian adsorpsi ion logam Cu(II) pada ester karboksimetil kitosan hasil sintesis

ISTIQAMAH, Nur, Dr. Dwi Siswanta, M.Eng

2010 | Tesis | S2 Ilmu Kimia

Telah dilakukan modifikasi kitosan menggunakan ester (etil kloroasetat)dan dipelajari ketahanan asam serta kemampuan mengadsorpsi ion logam Cu(II).Kitosan dihasilkan melalui deasetilasi kitin yang diisolasi dari cangkang udang.Parameter adsorpsi yang dipelajari meliputi penentuan pH optimum, kinetika adsorpsi, isoterm adsorpsi, ketahanan asam, pengaruh kation lain secara selektivitas, pengaruh berat adsorben dan penentuan mekanisme adsorpsi. Analisis Cu(II) sebelum dan sesudah proses adsorpsi dilakukan dengan menggunakan metode spektrofotometri serapan atom (SSA).Hasil penelitian menunjukkan bahwa kitosan dapat dimodifikasi dengan menggunakan ester (etil kloroasetat) yang dapat ditunjukkan dengan spektra IR.pH optimum adsorpsi Cu(II) berada pada pH 4. Tetapan laju adsorpsi kitosan dan ester karboksimetil kitosan pada pH optimum berturut-turut 0,099 dan 0,033 menit-1 dengan kapasitas adsorpsi masing-masing 98,93 dan 50,56 mg/g. Ester karboksimetil kitosan memiliki ketahanan dan kemampuan adsorpsi pada keadaan asam yang lebih baik daripada kitosan tanpa modifikasi. Adanya ion logam Ni(II) dalam adsorpsi Cu(II) tidak memberikan pengaruh yang signifikan hingga pada perbandingan mol Ni(II)/Cu(II)=2:1. Variasi berat adsorben menunjukkan persentase adsorpsi terbesar diperoleh pada 0,1 gram kitosan dan ester karboksimetil kitosan untuk volume larutan Cu(II) 20 mL dengan konsentrasi 150 ppm. Selain itu diketahui bahwa mekanisme adsorpsi Cu(II) oleh kitosan dan ester karboksimetil kitosan diprediksikan terjadi melalui pembentukan ikatan kompleks. Kata

Chitosan has been modified using ester (ethyl chloroacetate) and its stability toward acid solution for the adsorption of Cu(II) ions has been studied.Chitosan was prepared by deacetylating chitin isolated from shrimp shells.Adsorption parameters studied were the effect of pH, adsorption kinetic,adsorption isotherm, stability of ester- modified chitosan in acid solution, the effect of the other cations, effect of the adsorbent weight and adsorption mechanism.The analysis of Cu(II) ion before and after adsorption was done by using atomic absorption spectrometry (AAS).The result showed that chitosan can be modified with ester (ethyl chloroacetate) as confirmed by IR spectra. Optimum pH for the adsorption of Cu(II) was 4. The rate adsorption constant for chitosan and ester of carboxymethyl chitosan at optimum pH were 0.099 and 0.033 min-1 with the adsorption capacities were 98.93 and 50.56 mg/g Cu(II), respectively. Adsorption stability and capacity of ester of carboxymethyl chitosan was better than those of chitosan. The existence of Ni(II) in the Cu(II) solution did not significantly affect the adsorption of Cu(II) up to the mole ratio of Ni(II)/Cu(II) = 2:1. Variation of adsorbent weight showed that optimum percentage of adsorption was at the 0.1 g either for chitosan and ester of carboxymethyl chitosan, using Cu(II) solution of 20 mL with 150 ppm of concentration. The adsorption mechanism of Cu(II) on chitosan and ester of carboxymethyl chitosan was predicted to occur through complex formation.

Kata Kunci : Kitosan,Ester karboksimetil kitosan,Adsorpsi