Sintesis dan kajian regenerasi material hasil kalsinasi Zn/Al hidrotalsit serta aplikasinya sebagai adsorben Ag(S2O3)2

KARTIKASARI, Darwati, Prof. Dr. Sri Juari Santosa, M.Eng

2009 | Tesis | S2 Ilmu Kimia

Dalam penelitian ini telah dipelajari sintesis, perusakan struktur, dan regenerasi dalam air atas Zn/Al hidrotalsit. Hidrotalsit hasil sintesis, dan material hasil perusakan struktur dan regenerasi selanjutnya diuji coba sebagai adsorben untuk adsorpsi Ag(S2O3)23- dalam larutan. Sintesis hidrotalsit dilakukan dengan metoda pengendapan langsung melalui penambahan larutan NaOH 0,5 M ke dalam larutan campuran Zn (II) dan Al (III) dengan rasio molar 2:1 sampai keasaman larutan mencapai pH 7,2. Perusakan struktur hidrotalsit dilakukan dengan kalsinasi pada temperatur 500oC selama 2,5 jam. Regenerasi dilakukan terhadap material hasil kalsinasi dengan perendaman di dalam air selama 24 jam. Hasil penelitian menunjukkan bahwa kalsinasi pada temperatur 500oC selama 2,5 jam menyebabkan rusaknya struktur kristal hidrotalsit. Regenerasi dengan perendaman dalam air selama 24 jam belum mampu sepenuhnya mengembalikan struktur kristal hidrotalsit. Uji coba Zn/Al hidrotalsit dan material hasil perusakan dan regenerasi sebagai adsorben menunjukkan bahwa ketiganya mampu mengadsorpsi Ag(S2O3)23- dengan kapasitas masing-masing sebesar 6,41; 5,71; dan 5,73 × 10-4 mol/g.

It has been studied the synthesis, structure destruction, and regeneration in water of Zn/Al hydrotalcite. The synthesized hydrotalcite and materials obtained from structure destruction and its regeneration were tested as adsorbents for Ag(S2O3)23- in solution. Synthesis of hydrotalcite was done through direct precipitation by adding 0.5 M NaOH solution into a mixed solution of Zn (II) and Al (III) with molar ratio of 2:1 until medium acidity reached pH 7.2. The destruction of the structure of hydrotalcite was conducted by calcinations at 500oC for 2.5 hours. The regeneration was performed toward the calcinations product by soaking in water for 24 hours. The results showed that calcination at 500oC for 2.5 hours yielded the collapse of the crystalline structure of hydrotalcite. Regeneration through soaking in water for 24 hours was not able to restore the crystalline structure of hydrotalcite. The application of the hydrotalcite and the materials obtained from the structure destruction and its regeneration as adsorbents showed that they were able to adsorb Ag(S2O3)23- with adsorption capacity of 6.14, 5.71, and 5.73 × 10-4 mol/g, respectively.

Kata Kunci : Zn/Al hidritalsit, Kalsinasi, Regenerasi, Ag(S2O3)2, Adsorben Ag(S2O3)2