Kajian efek memori Mg/Al hydrotalcite dan aplikasinya sebagai adsorben ion kompleks perak tiosulfat (Ag(S2O3)2)

ZAMHARI, Taufik, Prof. Dr. Sri Juari Santosa, M.Eng

2009 | Tesis | S2 Ilmu Kimia

Dalam penelitian ini telah dipelajari sintesis, perusakan struktur, dan regenerasi dalam air atas Mg/Al hydrotalcite. Hydrotalcite hasil sintesis, dan material perusakan struktur dan regenerasi selanjutnya diujicoba sebagai adsorben untuk adsorpsi ion kompleks Ag(S2O3)23-. Sintesis Mg/Al hydrotalcite dilakukan dengan metode pengendapan langsung melalui penambahan larutan NaOH 0,5 M ke dalam larutan campuran Mg(II) dan Al(III) dengan rasio molar 2 : 1 sampai keasaman larutan mencapai pH 10,11. Perusakan struktur hydrotalcite dilakukan dengan kalsinasi pada temperatur 500 oC selama 2,5 jam. Regenerasi dilakukan terhadap material hasil kalsinasi dengan perendaman di dalam air selama 24 jam. Hasil penelitian menunjukkan bahwa struktur Mg/Al hydrotalcite yang dikalsinasi pada temperatur 500 oC selama 5 jam tidak mengalami kerusakan secara sempurna, tetapi hanya mengalami ketidakteraturan pada strukturnya. Regenerasi dengan perendaman dalam air selama 24 jam belum mampu sepenuhnya mengembalikan struktur kristal hydrotalcite. Ujicoba Mg/Al hydrotalcite dan material hasil perusakan dan regenerasi sebagai adsorben menunjukkan bahwa ketiganya mampu mengadsorpsi Ag(S2O3)23- dengan kapasitas masing – masing sebesar 3,93; 3,11; dan 3,16 x 10-4 mol/g.

The synthesis, structure destruction, and regeneration in water for Mg/Al hydrotalcite has been studied. The synthesized hydrotalcite and the materials obtained from the structure destruction and its regeneration were then tested as adsorbents for the adsorption of Ag(S2O3) 23- in solution. The synthesis of hydrotalcite was done through direct precipitation method by adding 0,5 M NaOH solution into a mixed solution of Mg(II) and Al(III) with molar ratio 2:1 until the medium acidity reached pH 10,11. The destruction of the structure of hydrotalcite was conducted by means of calcinations at temperature 500 oC for 2,5 hours. The regeneration was performed toward the calcinations product material through soaking in water for 24 hours. The result showed that the calcination at temperature 500 oC for 24 hours yielded an irregularity of the crystalline structure of Mg/Al hydrotalcite. Regeneration through soaking in water for 24 hours was not able to restore completely the crystalline structure of hydrotalcite. The application of the hydrotalcite and materials obtained from the structure destruction and its regenerations as adsorbents showed that they were able to adsorp Ag(S2O3)23- with adsorption capacity 3.93, 3.11, and 3.16x10-4 mol/g, respectively.

Kata Kunci : Mg/Al hydrotalcite,Efek memori,Kalsinasi,Regenerasi,Adsorpsi,memory efect, calcinations, regeneration, adsorption