Pengaruh ketersediaan oksigen, waktu dan suhu pemanasan terhadap karakteristik white charcoal bambu hitam (Gigantochloa atroviolaceae)

SUWARSONO, Gatot, Prof. Dr. Ir. Purmana Darmadji, M.Sc

2009 | Tesis | S2 Teknologi Hasil Perkebunan

Penelitian ini bertujuan untuk mengetahui pengaruh ketersediaan oksigen, waktu dan suhu pemanasan terhadap karasteristik arang putih bambu hitam. Bahan baku yang digunakan berupa bambu hitam yang diproses melalui pirolisis dengan parameter pengamatan meliputi kadar air, kadar abu, kadar volatil, fixed carbon, rendemen, kalori, kepadatan arang dan daya hantar listrik (DHL) terhadap rasio ketersediaan oksigen dalam tabung I, II, III dengan waktu pengamatan 1 jam, 9 Jam, 18 Jam dan pada suhu pemanasan 150ºC, 300ºC, 450ºC. Hasil penelitian menunjukkan bahwa pada tabung III dan lama waktu 18 jam dengan suhu pemanasan 4500C berpengaruh sangat nyata terhadap kadar air (1.156%). Pada tabung I lama waktu pemanasan 1 jam dengan suhu 1500C berpengaruh sangat nyata terhadap kadar Abu (2.542%). Pada tabung I lama waktu 18 jam dengan suhu 1500C berpengaruh sangat nyata terhadap kalori (6940 cal.g). Pada tabung I waktu 1 jam dengan suhu 150ºC berpengaruh sangat nyata terhadap kadar volatil (3.2564%). Pada tabung I lama waktu 1 jam dengan suhu 150ºC berpengaruh sangat nyata terhadap nilai rendemen (80.833%). Pada tabung III lama waktu 18 jam dengan suhu 150ºC berpengaruh sangat nyata terhadap kepadatan (96.133 Kg/cm²). Pada tabung I lama waktu 1 jam dengan suhu 150ºC berpengaruh sangat nyata terhadap fixed carbon (93.512%). Pada tabung III lama waktu 1 jam dengan suhu 300ºC tidak berpengaruh nyata terhadap daya hantar listrik (212 Ohm).

This research aim to know the influence is availibility of oxygen, time and warmup temperature to white carasteristic charcoal of black bamboo. Raw material used in the form of black bamboo processed by pirolisis with the perception parameter the rate water, dusty rate, volatil rate, fixed carbon, rendemen, calorie, density of charcoal and energy pass the electrics (DHL) to ratio is availibility of oxygen in tube I, II, III with the perception time 1 clock, 9 clock, 18 clock and warm-up temperature 150ºC, 300ºC, 450ºC. Result of research indicate that tube III and time depth 18 clock with the warm-up temperature 450ºC having effect on very real to rate water (1.156%). At tube I of time depth warm-up 1 clock with the temperature 1500C having an effect on very real to dusty rate (2.542%). At tube I of time depth 18 clock with the temperature 1500C having effect on very real to calorie (6940 cal/g). At tube I of time 1 clock with the temperature 150ºC having effect on very real to rate volatil (3.2564%). At tube I of time depth 1 clock with the temperature 150ºC having effect on very real to value rendemen (80.833%). At tube III of time depth 18 clock with the temperature 150ºC having effect on very real to density (96.133 Kg/cm²). At tube I of time depth 1 clock with temperature 150ºC having effect on very real to fixed carbon (93.512%). At tube III of time depth 1 clock with the temperature 300ºC do not differ the reality to energy pass the electrics (212 Ohm).

Kata Kunci : Bahan baku, karbonisasi, pirolisis, arang putih, rasio ketersediaan oksigen, waktu dan suhu pemanasan, Raw material, carbonisasi, pirolisis, white charcoal, ratio water, time and warm-up temperature