Kajian efek-efek termo-mekanik dari main-chain liquid crystal elastomer (MC-LCE)

MONGKITO, Vivi Hastuti Rufa, DR. Yusril Yusuf, M.Eng

2009 | Tesis | S2 Ilmu Fisika

Te lah dilakukan penelitian sifat-sifat termo-mekanik pada main-chain liquid crystal elastomer (MC-LCE), dengan perbedaan konsentrasi cross-linker 2.5 %, 6 % d an 12 %, sebagai fungsi suhu akibat proses pemanasan (heating) dan pending inan (cooling). Bila suhu meningkat, panjang MC-LCE secara monoton menyusut sejajar terhadap arah direktor, n, sementara MC-LCE mengembang teg ak lurus terhadap arah n dengan berkurang secara cepat di sekitar suhu transisi ne matik-isotropik, Tni, selama proses pemanasan. Setelah pendinginan, semua sam pel kembali ke bentuk semula. Kontraksi maksimum meningkat dengan m eningkatnya konsentrasi cross-linking. Kontraksi maksimum dari MC-LCE deng an konsentrasi cross-linker 12 % adalah sekitar 120 %. Histeresis dari perubaha n panjang relatif dan perubahan volume dari MC-LCE dikaji sebagai fungsi suhu. Perubahan panjang relatif dan perubahan volume dari MC-LCE me nunjukkan histeresis yang signifikan pada transisi nematik-isotropik selama proses pemanasan dan pendinginan.

Thermo-mechanical effects of dry main-chain liquid crystal elastomers (MC-LCEs) with the different concentration of crosslinkers 2.5%, 6 % and 12 %, as a function of temperature has been investigated. As temperature increase, the length of MC-LECs monotonically shrinks parallel to the director, n, while it expands perpendicular to n, with a somewhat faster decrease in the vicinity of the apparent nematic-isotropic transition temperature, Tni, during the processes on heating. After cooling, all samples return to their original shape. The maximum contraction increases with increasing cross-linking concentration. The maximum contraction of MC-LCEs with concentration of crosslinker of 12 % is about 120%. The hystereses of relative length and volume changes of MC-LCEs are studied as a function of temperature. The relative length and volume changes of MC-LCEs shows significant hystereses at nematic-isotropic transition during the processes on heating and cooling.

Kata Kunci : Main,chain liquid crystal elastomers (MC,LCEs),Efek,efek termomekanik, Main-chain liquid crystal elastomers (MC-LCEs), thermo-mechanical effects