Pengaruh perlakuan asam nitrat terhadap karakter zeolit alam Klaten

UTAMININGSIH, Raden Rara, Prof. Dra. Wega Trisunaryanti, MS, Ph.D.Eng

2009 | Tesis | S2 Ilmu Kimia

Telah dilakukan penelitian yang bertujuan untuk mempelajari pengaruh perlakuan asam nitrat dengan variasi konsentrasi dan waktu refluks terhadap dealuminasi, dekationisasi, keasaman, dan kristalinitas zeolit alam Klaten. Dalam penelitian ini sampel zeolit alam direfluks pada suhu 90°C dengan asam nitrat pada variasi konsentrasi 1M, 2M, 3M, 4M, 5M serta waktu refluks 30, 60 dan 120 menit. Karakterisasi sampel zeolit meliputi dealuminasi, dekationisasi, keasaman dan kristalinitas masing-masing berturut-turut dianalisis dengan metode Infra Red spectroscopy (IR) dengan mengamati bilangan gelombang gugus TO4(rumus) (T = Al atau Si) pada daerah 1000-1100 cm-1(simbol), Atomic Absorption Spectroscopy (AAS), gravimetri melalui adsorpsi amonia, dan difraksi sinar-X (XRD). Hasil penelitian menunjukkan bahwa perlakuan asam nitrat terhadap zeolit alam dengan variasi konsentrasi dan waktu refluks menyebabkan dealuminasi yang ditandai dengan terjadinya pergeseran bilangan gelombang puncak TO4(rumus) ke arah yang lebih tinggi, meningkatkan keasaman, menurunkan kandungan logam Na dan meningkatkan kristalinitas zeolit alam. Perlakuan HNO3(rumus) dengan konsentrasi 5M dan waktu refluks 0,5 jam menghasilkan keasaman total zeolit tertinggi yaitu 5,19 mmol/gram dan kandungan logam Na terendah yaitu 4,4 mg /g zeolit.

The effect of nitric acid treatment in variation of concentration and reflux time on dealumination, acidity, decationization of Na, and cristalinity of natural zeolite from Klaten have been studied. In this research the natural zeolite samples were refluxed in variation of concentration 1M, 2M, 3M, 4M and 5M of nitric acid at 90°C at reflux time of 30, 60 and 120 min. Characterization of zeolite samples included dealumination, acidity, decationization of Na, and crystalinity was analyzed by Infra Red Spectroscopy (IR) at wave number of TO4(formula) groups (T = Al or Si) on 1000-1100 cm-1(symbol) , gravimetry with adsorption of amonia, Atomic absorption Spectroscopy (AAS), X-ray difraction (XRD) method, respectively. The results towards natural zeolite showed that nitric acid treatment in variation of concentration and reflux time caused dealumination indicated by increasing wave number shifting of TO4(forumula) groups, increased acidity, decreased concentration of Na, and increased crystallinity. The treatment of nitric acid (HNO3)(formula) in concentration 5M and reflux time 30 min increased highest total acidity i.e. 5.19 mmol/gr and lowest concentration of Na i.e. 4.4 mg/g zeolite.

Kata Kunci : Asam nitrat, zeolit alam Klaten, nitric acid, natural zeolite from Klaten