Studi adsorpsi zat warna metil violet oleh abu dasar batu bara

WIYONO, Heri, Dr. rer.nat. Nurul Hidayat A, M.Si

2009 | Tesis | S2 Ilmu Kimia

Telah dilakukan penelitian mengenai adsorpsi zat warna metil violet oleh abu dasar batu bara. Penelitian ini bertujuan untuk mempelajari kemampuan abu dasar batu bara dalam mengadsorpsi metil violet. Beberapa parameter adsorpsi yang dipelajari adalah pH medium, massa adsorben, kinetika, energi dan kapasitas adsorpsi. Karakterisasi abu dasar batu bara dilakukan dengan Gas Sorption Analyzer (GSA), difraksi sinar-X (X-RD) dan spektrofotometer inframerah (FTIR). Adsorpsi metil violet dipelajari dengan variasi pH, massa adsorben, waktu kontak dan konsentrasi awal. Metil violet yang teradsorpsi dihitung secara kuantitatif dengan menggunakan Spektrofotometer Sinar Tampak. Hasil XRD dan FTIR menunjukkan bahwa senyawa yang t erkandung dalam abu dasar batu bara memiliki situs atif yang dapat digunakan sebagai adsorben dalam proses adsorpsi yaitu SiO2 (kuarsa) dan Al2O3 (mullit). Hasil GSA menunjukkan luas permukaan spesifik meningkat dari 8,4 4 m2/g menjadi 10,51 m2/g. Kondisi optimum adsorpsi terhadap 30 mL larutan metil violet 10 ppm terjadi pada pH 8, waktu kontak 60 menit dan konsentrasi 40 mg/L untuk setiap 2 g abu dasar. Hasil penelitian menunjukkan bahwa adsorpsi metil violet oleh abu dasar batu bara merupakan adsorpsi orde satu dengan konstanta laju 2,04 × 10-2 detik-1, kapasitas adsorpsi 2,49 × 10-6 mol/g dan energi adsorpsi 46,36 kJ/mol.

A reseach about the adsorption of methyl violet on coal bottom ash has been conducted. This research was aimed to examine the ability of bottom ash in adsorbing methyl violet. Some adsorption parameters such as pH med ium, kinetics, energy and capacity were examined in the adsorption process. The characterization of coal bottom ash was determined using the Gas Sorption Analyzer (GSA), X-Ray Diffraction (X-RD) and Infrared Spectrometer (FTIR). The adsorbed methyl violet was measured quantitatively based on the concentration of methyl violet using the UV-visible spectrophotometer. The results of FTIR and X-RD showed that the compounds found in coal bottom ash had active sites that can be used as adsorbent in the ad sorption process, and these compounds are SiO2 and Al2O3. The result of GSA showed that specific surface area increased from 8.44 m2/g to 10.51 m2/g. Optimal adsorption conditions were achieved in pH 8, contact time 60 minutes and me thyl violet concentration of 40 mg/L for every 2 g of bottom ash. This research showed that the adsorption of methyl violet by bottom ash is a first order with adsorption rate constant of 2.04 × 10-2 s-1, adsorption capacity 2.49 × 10-6 mole/g and energy of adsorption of 46.36 kJ/mole, respectively.

Kata Kunci : abu dasar batubara, metil violet, adsorpsi, coal bottom ash, methyl violet, adsorption