Pengaruh perlakuan larutan asam klorida terhadap karakter zeolit alam Klaten

PADI, Prof. Dra. Wega Tri Sunaryanti, MS., M.Eng., Ph.D

2009 | Tesis | S2 Ilmu Kimia

Telah dipelajari pengaruh perlakuaan larutan asam klorida terhadap karakter zeolit alam Klaten. Tujuan penelitian ini adalah mempelajari pengaruh perlakuan larutan asam klorida pada berbagai konsentrasi (1, 2, 3, 4, dan 5 M) dan waktu refluks (30, 60, dan 120 menit) terhadap dealuminasi, dekationisasi logam Na, keasaman, dan kristalinitas zeolit alam Klaten. Karakterisasi sampel zeolit meliputi dealuminasi, dekationisasi logam Na, keasaman, dan kristalinitas yang masing-masing berturut-turut dianalisis dengan metode Spektroskopi Infra Merah dengan mengamati daerah bilangan gelombang gugus TO4 (T = Al atau Si) pada daerah 1000-1100 cm-1, Atomic Absorption Spectroscopy (AAS), gravimetri dengan menggunakan uap amonia, dan difraksi sinar –X (XRD). Hasil penelitian menunjukkan bahwa pengaruh perlakuan larutan asam klorida pada konsentrasi 1, 2, 3, 4, dan 5 M dengan waktu refluks 30, 60, dan 120 menit terhadap zeolit alam Klaten menyebabkan dealuminasi yang ditandai dengan naiknya rasio Si/Al secara kualitatif. Perlakuan larutan asam klorida pada konsentrasi 5 M dengan waktu reflluks 120 menit, menyebabkan dekationisasi logam Na hingga 37,21% dan meningkatkan kristalinitas zeolit alam. Perlakuan larutan asam klorida pada konsentrasi 1 M dengan waktu refluks 30 menit menaikkan keasaman zeolit alam hingga 77,27%.

The effect of hydrochloric acid solution treatment towards characters of natural zeolite from Klaten has been studied. The purpose of this research was to study the effect of the acid treatment in variation of concentrations (1, 2, 3, 4, and 5 M) and reflux times (30, 60, and 120 min.) towards dealumination, decationization of Na, acidity, and cristalinity of zeolite samples. The characterization of zeolite samples included dealumination, decationization of Na, acidity and cristalinity were analyzed by Infra Red Spectroscopy, Atomic Absorption Spectroscopy (AAS), gravimetric using ammonia vapor, and X-ray difraction (XRD) methods, respectively. The results of this research showed that the hydrochloric acid solution treatment at concentrations of 1, 2, 3, 4, and 5 M with reflux times of 30, 60, and 120 min. towards natural zeolite from Klaten caused dealumination that indicated by the qualitatively increase of Si/Al ratio. The hydrochloric acid solution treatment at concentration of 5 M with reflux time of 120 min. caused decationization of Na up to 37.21% and increased the natural zeolite cristalinity. The hydrochloric acid solution treatment at concentration of 1 M with reflux time of 30 min. increased the natural zeolite acidity up to 77.27%.

Kata Kunci : Perlakuan larutan HCL,Zeolit alam,Karakterisasi