Pengaruh Recharging Fluorida pada Resin Komposit tipe Nanofil/er terhadap Perlekatan Streptococcus Mutans dan Kekuatan Kompresi

ASTUTI, Ni Kadek Ari, Dr. drg. Widjijono, SU

2008 | Tesis | S2 Ilmu Kedokteran Gigi

Akumulasi bakteri terutama Streptococcus mutans pada permukaan bahan restorasi dapat menyebabkan teijadinya karies sekwtder. Aplikasi topikal fluorida pada permukaan bahan restorasi diketahui dapat menambah kandungan fluorida dalam bahan sehingga mencegah teijadinya karies sekunder. Hal ini sangat dibutuhkan selama tidak menimbulkan efek yang merugikan terhadap sifat fisik dan mekanik bahan. Penelitian ini bertujuan mengetahui pengaruh recharging fluorida pada resin komposit tipe nanofi//er terhadap perlekatan Streptococcus mutans dan kekuatan kompresi. Jumlah sampel penelitian adalah 48 sampel resin komposit tipe nanofiller (Tetric EvoCeram, Vivadent lvoclar, Schaan, Liechtenstein). Dua puluh empat sampel diambil secara acak untuk uji perlekatan Streptococcus mutans dan 24 sampel untuk uji kompresi. Masing-masing dibagi dalam 4 sub kelompok terdiri dari 6 spesimen. Aplikasi topikal NaF dengan konsentrasi 1%, 2%, 3% pada 3 kelompok dan pada 1 kelompok tidak dilakukan recharging NaF (kontrol). Kelompok yang akan diuji perlekatan Streptococcus mutans direndam dalam larutan saliva buatan dan Streptococcus mutans, diinkubasi selama 24 jam pada suhu 37°C lalu diinokulasikan pada Plate count agar (PCA). Koloni yang terbentuk dihitung menggunakan alat colony counter. Pada kelompok uji kompresi dilakukan pengukuran kekuatan kompresi dengan menggunakan Tokyo universal testing machine. Seluruh data yang diperoleh dianalisis menggunakan ANOVA satu jalur. Hasil analisis varian menunjukkan bahwa recharging fluorida berpengaruh terhadap perlekatan Streptococcus mutans dan juga kekuatan kompresi bahan (p<0,05). Kesimpulan dari penelitian ini adalah recharging fluorida pada resin komposit nanofil/er berpengaruh terhadap perlekatan Streptococcus mutans dan kekuatan kompresi. Kata kunci : Recharging fluorida, resin komposit tipe nanofil/er, Streptococcus mutans, kekuatan kompresi

Accumulation of bacteria such as Streptococcus mutans on restorative materials can lead to secondary dental caries. Topical application of fluoride on the surface of restoration materials known to be able to increase the fluoride content in materials, preventing secondary caries. This is highly desirable as long as it does not have detrimental effect on physical and mechanical characteristics of the materials. The study aims at finding out the effect of fluoride recharging in nanofiller type composite resin on the adhesion of Streptococcus mutans and compression strength. The research took 48 samples of nanofiller type composite resin (Tetric Evo Ceram, Vivadent Ivoclar, Schaan, Liechtenstein). Twenty four samples were randomly selected for adhesion test of Streptococcus mutans and the other 24 were for compression test. The two groups divided into four sub groups consisting of six specimens. In each groups, topical application of NaF with the concentration of 1%, 2% and 3% was done on three sub groups, but no NaF recharging was done on the other one (control) sub group. The Streptococcus mutans adhesion test group was soaked in the artificial saliva liquid and Streptococcus mutans, was incubated for 24 hours at 37°C, and was innoculated on the Plate count agar (PCA). The colonies formed were counted using a colony counter device. In the compression test group, compressive strength measurement is done using Tokyo universal testing machine. All data collected were analyzed using one-way ANOVA. The analysis of variance result showed that fluoride recharging had effect on the adhesion of Streptococcus mutans as well as the compression strength of materials (p<0.05). The study concludes that flouride recharging in nanofiller tipe composite resin has effects on adhesion of Streptococcus mutans and the compression strength. Keywords : fluoride recharging, nanofiller type composite resin, Streptococcus mutans, compression strength.

Kata Kunci : Recharging fluorida, Resin komposit tipe nonfiller, Streptococcus mutans, Kekuatan kompresi