Pengaruh Sr atau TiB terhadap kekuatan tarik, kekerasan dan struktur mikro paduan Al-6 persen dengan metode pembekuan searah

BASORI, Imam, Dr. Suyitno, ST.,M.Sc

2007 | Tesis | S2 Teknik Mesin

Penelitian ini bertujuan untuk mengetahui pengaruh Sr atau TiB terhadap kekuatan tarik, kekerasan dan struktur mikro paduan Al-6%Si pada proses pembekuan searah (directional solidification). Proses pembekuan searah dilakukan pada paduan Al-6%Si, Al-6%Si+Sr dan Al-6%Si+TiB. Spesimen dalam cetakan stainless steel dengan isolasi tanah liat dilebur menggunakan dapur listrik sampai temperatur 700 0C, kemudian dilakukan proses pembekuan searah. Struktur mikro diamati menggunakan mikroskop optik sedangkan kekerasan material diuji menggunakan metode Brinell. Spesimen uji tarik mengacu pada standar ASTM B 557M. Hasil penelitian menunjukkan bahwa proses pembekuan searah serta penambahan Sr atau TiB sangat berpengaruh terhadap struktur mikro paduan Al- 6%Si. Pembekuan searah mengubah struktur butir equiaxed menjadi struktur kolumnar. Penambahan Sr akan memperbaiki orientasi butir kolumnar dan penambahan TiB tidak terlalu signifikan mempengaruhi pembentukan struktur kolumnar. Kekuatan tarik dan kekerasan Brinell paduan Al-6%Si meningkat dengan penambahan Sr atau Tib.

Aim of this work is to study influence of Sr or TiB addition on mechanical properties and microstructure of Al-6%Si on directional solidification process. Material of Al-6%Si, Al-6%Si+Sr and Al-6%Si+TiB with clay isolation were melted in electric crucible at 700 0C and be solidified by directional solidification process. The microstructure change were studied by optical microscope and the hardness measurements were used Brinell hardness test. The specimens of tensile test are designated in ASTM B 557M standards. The results show that the directional solidification process and addition of Sr or TiB in Al-6%Si alloys modify the morphology of microstructure. The experiment result demonstrate that directionality of columnar structure are promote by the addition of Sr. The addition of Tib is not significant to promote this directionality. The directinonal solidification process with addition of Sr and Tib also result in increase tensile strength and Brinell Hardness number.

Kata Kunci : Pembekuan Searah,Struktur Kolumnar,Sr atau TiB,directional solidification, columnar, Al-6%Si