Pengaruh kekasaran permukaan resin komposit Packable dengan Recharging Fluoride terhadap pelekatan Streptococcus mutans

NURMALASARI, Afrida, Dr.drg. Widjijono, SU

2007 | Tesis | S2 Ilmu Kedokteran Gigi

Kekasaran permukaan resin komposit packable, mempengaruhi kecepatan akumulasi dan pertumbuhan Streptococcus mutans, sehingga menyebabkan terjadinya karies berulang. Aplikasi topikal fluorida ke permukaan bahan restorasi diketahui dapat mencegah karies berulang. Penelitian ini bertujuan mengetahui pengaruh kekasaran permukaan bahan resin komposit packable dengan recharging fluoride terhadap pelekatan Streptococcus mutans. Penelitian ini dilakukan menggunakan empat kelompok resin komposit packable dengan berbagai variasi kekasaran permukaan. Resin komposit packable disterilkan 10 menit dengan sinar ultraviolet, kemudian tiga kelompok (kekasaran rendah, sedang, dan tinggi) dilakukan recharging fluoride menggunakan gel SnF2 0,4%, dan satu kelompok kekasaran rendah tidak dilakukan recharging fluoride (kontrol). Semua kelompok selanjutnya direndam dalam larutan saliva buatan dan Streptococcus mutans, diinkubasi selama 24 jam pada suhu 37°C. Setelah 24 jam, Streptococcus mutans diinokulasikan pada Plate Count Agar (PCA), dan diinkubasi selama 24 jam pada suhu 37°C. Koloni yang terbentuk dihitung menggunakan alat colony counter dan dianalisis menggunakan One-way ANOVA. Hasil analisis varian menunjukkan bahwa recharging fluoride berpengaruh terhadap penurunan pelekatan Streptococcus mutans (p<0,05). Kesimpulan dari penelitian ini adalah recharging fluoride pada resin komposit packable berpengaruh terhadap penurunan pelekatan Streptococcus mutans. Resin komposit packable kekasaran permukaan tinggi dengan recharging fluoride, menunjukan pelekatan Streptococcus mutans yang paling sedikit pada permukaan resin komposit packable.

Surface roughness of packable resin composite effecting the rate of acumulation and the growth of Streptococcus mutans, which caused secondary caries. Fluoride topical application on the surface of restoration material known as preventive of secondary caries. This research aim to investigate the effect of surface roughness on material of packable resin composite in the fluoride recharging to adhesion of Streptococcus mutans. This research use four groups of packable resin composite with several variation of surface roughness. Packable resin composite sterilized for ten minutes with ultraviolet light, after that three groups (low, moderate, and high roughness) treatened fluoride recharging using SnF2 0,4% gel, and one group without fluoride recharging treatened (control). All the groups, furthermore being soaked in the saliva artificial liquid and Streptococcus mutans for 24 hours on temperature 37°C. After 24 hours, the Streptococcus mutans being innoculated on the Plate Count Agar (PCA), and being incubated for 24 hours on temperature 37°C. The colony that formed counted using colony counter tool and analysed using Oneway ANOVA test. The varian analysis result showed that fluoride recharging effect significant on the adhesion decrease of Streptococcus mutans (p<0,05). The conclusion of this study is fluoride recharging on the packable resin composite effect on adhesion decrease of Streptococcus mutans. The high value of packable resin composite surface roughness with fluoride recharging, there showed the most smidgen of the Streptococcus mutans adhesion on the surface of packable resin composite.

Kata Kunci : Resin Komposit Packable,Fluoride,Pelekatan,Packable resin composite, surface roughness, fluoride recharging, Streptococcus mutans