Variasi Lama Terpapar Resin Komposit Sinar-Tampak Dengan Penambahan 0,17 Persen b/b Kamforoquinon Terhadap Kekerasan dan Jumlah Ikatan Rangkap Karbon (C=C) :: Penelitian Eksperimental Laboratorium

FATMAWATI, Dwi Warna Aju, Dr.drg. Widjijono, SU

2005 | Tesis | S2 Ilmu Kedokteran Gigi

Tujuan penelitian ini dibatasi pada pengukuran kekerasan dan jumlah sisa ikatan rangkap karbon (C=C) sebagai dampak polimerisasi akibat pengaruh variasi lama terpapar sinar dengan penambahan 0,17% b/b kamforoquinon pada resin komposit sinar-tampak. Penelitian ini merupakan penelitian eksperimental laboratorium. Sampel dibagi menjadi 5 kelompok yaitu kelompok terpapar 30 detik, 60 detik, 90 detik, 120 detik dan kontrol. Masing-masing kelompok terdiri dari 7 sampel (n=7). Kelompok perlakuan setelah terpapar sinar diberi kamforoquinon 0,17% b/b dan di sinar-tampak. Semua kelompok dilakukan uji kekerasan menggunakan alat Vickers Hardness dan pengukuran jumlah sisa ikatan rangkap karbon (C=C) resin komposit sinar-tampak menggunakan alat FTIR-Spektroskopi. Rerata kekerasan terbesar pada kelompok kontrol sebesar 4,48 ± 0,08 VHN (Vickers Hardness Number) dan kekerasan terkecil pada kelompok terpapar sinar 120 detik 3,14 ± 0,17 VHN, secara statistik menunjukkan perbedaan yang bermakna (P<0,05). Rerata jumlah sisa ikatan rangkap karbon (C=C) terkecil pada kelompok kontrol sebesar 0,02214 ± 0,003132 cm2 dan rerata terbesar pada kelompok terpapar sinar 120 detik 0,02657 ± 0,001272 cm2, secara statistik juga menunjukkan perbedaan yang bermakna (P<0,05). Jumlah sisa ikatan rangkap karbon (C=C) resin komposit sinar-tampak menunjukkan peningkatan akibat terpapar sinar, sisa ikatan rangkap karbon (C=C) diukur setelah penambahan 0,17% b/b dan dilakukan penyinaran dengan sinar-tampak. Besarnya peningkatan pada kelompok perlakuan dibanding kelompok kontrol secara berturut-turut dengan lama paparan sinar 30 detik, 60 detik, 90 detik dan 120 detik yaitu 4,52%; 5,83%; 13,6% dan 20%.

The objective of this research has been limited to measuring of hardness and amount of remaining double bonds carbon as effect of polymerization that results the influence of variation light exposured with an addition of 0,17% b/b camphoroquinone of composite resin visible light-cured. This research was a laboratory experimental research. Sample was divided into 5 groups which were the exposure of 30 second, 60 second, 90 second, 120 second and control. Each group consists of 7 samples (n=7). After sample in each group was exposed to light, it was gave 0,17% b/b camphoroquinone , and then cured. All groups were tested for their hardness using Vickers Micro Hardness and for the amount of remaining double bonds carbon of composite resin visible light-cured using FTIR-Spectroscopy. The highest average of hardness in control group, i.e., 4,48 ± 0,08 VHN (Vickers Hardness Number) and the lowest in group exposed for 120 second, i.e., 3,14 ± 0,17 VHN, there were a significant difference (P<0,05). The amount of remaining double bonds carbon (C=C) showed the lowest mean at control group 0,02214 ± 0,003132 cm2, and the highest at 120 second group 0,02657 ± 0,001272 cm2, there were a significant difference (P<0,05). The amount of remaining double bonds carbon (C=C) composite resins visible light-cured was showed an improvement that results from exposure to light with an addition of 0,17% b/b camphoroquinone after cured. Level of improvement at variation group compared to control group at 30 second, 60 second, 90 second and 120 second, which were 4,52%, 5,83%, 13,6% and 20% respectively.

Kata Kunci : Resin Komposit Sinar Tampak,Kamforoquin,Kekerasan, Composite resins visible light-cured, camphoroquinone, hardness, double bonds carbon