SIFAT PAPAN KOMPOSIT PELEPAH PINANG (Areca sp) DENGAN PEREKAT BERBASIS ASAM SITRAT
Katharina Nesi Mau, Prof.Dr.Agr.Sc.Ragil Widyorini,S.T.,M.T.,IPU ; Prof.Ir.Tibertius Agus Prayitno, M.For.Ph.D
2025 | Tesis | S2 Ilmu Kehutanan
Pelepah pinang merupakan salah satu bahan baku non-kayu yang berpotensi untuk dijadikan sebagai bahan baku papan komposit yang ramah lingkungan. Penggunaan partikel pelepah pinang disertai penambahan serat pelepah pinang diduga dapat meningkatkan sifat fisika dan mekanika papan yang dihasilkan. Penelitian ini bertujuan untuk mengevaluasi pengaruh komposisi bahan dan jumlah asam sitrat terhadap sifat fisika dan mekanika papan komposit. Bahan yang digunakan, yaitu partikel pelepah pinang dan serat pelepah pinang dengan perekat asam sitrat 10%, 15%, dan 20%. Papan komposit dengan ukuran 25,5x25,5x1 cm3 dan target kerapatan 0,8 g/cm3, dibuat dengan komposisi partikel:serat pelepah pinang 100:0, 90:10, 80:20, dan 70:30 g/g%. Pengempaan dilakukan pada suhu 1800C selama 10 menit dengan tekanan spesifik 3 MPa. Pengujian sifat fisika dan mekanika papan berdasarkan standar JIS A 5908-2003. Hasil penelitian menunjukan komposisi bahan berpengaruh nyata pada tarah uji 0,01 terhadap kerapatan, keteguhan rekat internal, modulus patah dan modulus elastisitas, sedangkan jumlah asam sitrat berpengaruh nyata terhadap taraf uji 0,01 terhadap kadar air, pengembangan tebal dan penyerapan air.
Areca palm frond is a potential non-wood raw material
for producing environmentally friendly composite boards. The addition of areca palm
frond fiber is hypothesized to enhance the resulting physical and mechanical properties
of composite board. This study aimed to evaluate the effects of material composition
and citric acid content on the physical and mechanical properties of the composite
board made from areca palm frond. The materials used were areca palm fronds particles
and fibers, bonded with citric acid at adhesive content of 10%, 15%, and 20%. Composite
boards were manufactured with dimensions of 25.5 × 25.5 × 1 cm³ and a target density
of 0.8 g/cm³, using particle to fiber compositions of 100:0, 90:10, 80:20, and 70:30
(w/w%). Hot pressing was performed at 180°C for 10 minutes under a specific pressure
of 3 MPa. Physical and mechanical properties of the board were
evaluated based on the Japanese Industrial Standar (JIS) A 5908-2003, covering density,
moisture content, thickness swelling, water absorption, surface roughness, internal
bonding strengh, modulus of rupture, and modulus of elasticity. The results showed
that the composition of the material had a significant effect on density, internal
bonding strength, modulus of rupture, and modulus of elasticity at the test level
of 0.01, while citric acid content had a significant effect on water content, thickness
swelling, and water absorption at the test level of 0.01.
Kata Kunci : asam sitrat, komposisi, partikel pelepah pinang, serat pelepah pinang, sifat papan komposit / citric acid, compositions, areca palm fornd particle, areca palm frond fiber, properties composite board