STUDI EKSPERIMENTAL MENGENAI KEMAMPUAN ADSORPSI BATUBARA INDONESIA TERHADAP CO2

Barlin, Prof. Dr. Ir. Indarto, DEA

2009 | Tesis | S2 Teknik Mesin

Penelitian ini bertujuan untuk mengetahui pengaruh ukuran partikel dan peringkat batubara terhadap kemampuan adsorpsi CO2. Empat jenis batubara telah digunakan yang berasal dari Sumatera Selatan dan Kalimantan Timur. Ukuran partikel batubara terdiri dari 0,075 mm; 0,15 mm; 0,3 mm; 0,4 mm; 0,6 mm dan 1,0 mm. Peringkat batubara bervariasi dari lignite, sub bituminous, high volatile biuminous C (HVBC) dan high volatile bituminous B (HVBB). Pengujian kemampuan adsorpsi CO2 dilakukan dengan metode volumetrik pada tekanan CO2 antara 10 - 60 bar dan temperatur sistem 40oC. Kemampuan adsorpsi CO2 menurun dengan bertambahnya ukuran partikel dan meningkat dengan meningkatnya peringkat batubara. Penurunan kemampuan adsorpsi CO2 akibat peningkatan laju adsorpsi dengan bertambahnya ukuran partikel. Peningkatan kemampuan adsorpsi CO2 akibat bertambahnya kandungan karbon dan berkurangnya tingkat kelembaban.

The aim of the research is to study influence of particle size and coal rank on CO2-adsorption capacity. Four type of coals were examined in this research, 2 type from South Sumatera and the other from East Kalimantan. Particle sizes were varied from 0.075 mm, 0.15 mm, 0.3 mm, 0.4 mm, 0.6 mm and 1.0 mm. The coal ranks varied from lignite, sub bituminous, high volatile biuminous C (HVBC) dan high volatile bituminous B (HVBB). The measurement of CO2-adsorption capacity used volumetric method and were conducted at pressure between 10 up to 60 bar and 40oC of system temperature. CO2-adsorption capacity decreased with increasing particle size and increased with increasing coal rank. The decreasing relative CO2-adsorption capacity as well as the increasing adsorption rate with increasing particles size. The increasing relative CO2-adsorption capacity as well as the increasing carbon contents and the decreasing moisture contents.

Kata Kunci : batubara, karbondioksida (CO2), adsorpsi, metode volumetrik