Kajian Struktur Kristal dan Sifat Optik Green-Synthesized Nanokomposit CoFe?O?/rGO

Rafli Fathoriq, Prof. Dr.Eng. Edi Suharyadi, S.Si., M.Eng.

2025 | Skripsi | FISIKA

Telah dilakukan penelitian mengenai nanokomposit CoFe?O?/rGO yang disintesis menggunakan metode alternatif green synthesis menggunakan ekstrak Moringa Oleifera dan Amaranthus Viridis yang dikaji struktur kristal dan sifat optiknya. Hasil analisis menggunakan X-Ray Diffraction menunjukkan nilai parameter kisi yang diperoleh dari sintesis nanopartikel CoFe?O? dan nanokomposit CoFe?O?/rGO dengan perbandingan massa 5:5, keduanya sebesar (8,2 ± 0,1) Å serta ukuran kristalit yang didapatkan adalah (9,8 ± 0,1) dan (9,3 ± 0,3) nm. Hasil analisis Fourier Transform Infra-Red Spectroscopy menunjukkan adanya gugus fungsi Fe-O dan Co-O pada nanopartikel CoFe?O? dan nanokomposit CoFe?O?/rGO yang mengindikasikan keberhasilan sintesis pada nanopartikel dengan metode green synthesis. Pada Hasil analisis spektroskopi Ultraviolet-Visible menunjukkan puncak serapan sampel rGO, CoFe?O?, dan CoFe?O?/rGO ada pada panjang gelombang 281, 209, dan 224 nm serta diperoleh nilai celah energi yang didapatkan adalah (3,43±0,04), (3,7±0,1), dan (3,1±0,1) eV. Dari hasil analisis yang didapatkan, terdapat penurunan ukuran kristalit, kristalinitas, dan celah energi pada nanokomposit CoFe?O?/rGO perbandingan massa 5:5 menggunakan metode green syntesis.

Research has been conducted on CoFe?O?/rGO nanocomposites synthesized using an alternative green synthesis method using Moringa Oleifera and Amaranthus Viridis extracts which were studied for their crystal structure and optical properties. The results of the analysis using X-Ray Diffraction showed that the lattice parameter values obtained from the synthesis of CoFe?O? nanoparticles and CoFe?O?/rGO nanocomposites with a mass ratio of 5:5, both were (8.2 ± 0.1)Å and the crystallite sizes obtained were (9.8 ± 0.1) and (9.3 ± 0.3) nm. The results of Fourier Transform Infra-Red Spectroscopy analysis showed the presence of Fe-O and Co-O functional groups in CoFe?O? nanoparticles and CoFe?O?/rGO nanocomposites which indicated the successful synthesis of nanoparticles using the green synthesis method. Ultraviolet-Visible spectroscopy analysis results show the absorption peaks of rGO, CoFe?O?, and CoFe?O?/rGO samples at wavelengths of 281, 209, and 224 nm and the obtained energy gap values are (3.43 ± 0.04), (3.7 ± 0.1), and (3.1 ± 0.1) eV. From the analysis results obtained, there is a decrease in the crystallite size, crystallinity, and energy gap in the CoFe?O?/rGO nanocomposite with a mass ratio of 5:5 using the green synthesis method.

Kata Kunci : Amaranthus Viridis, CoFe?O?/rGO, green synthesis, Moringa Oleifera, Nanokomposit