GREEN SYNTHESIZED NANOKOMPOSIT Fe3O4/rGO SEBAGAI FOTOKATALIS LIMBAH RHODAMINE B

Iska Novia Ramadhani, Prof. Dr.Eng. Edi Suharyadi, S.Si., M.Eng.

2025 | Skripsi | FISIKA

Pada penelitian ini berhasil dilakukan proses green synthesis serta diketahui struktur kristal, sifat magnetik, dan tingkat absorpsi nanokomposit Fe3O4/rGO, juga pengaruh massa katalis terhadap degradasi limbah rhodamine b (RhB). Metode yang digunakan untuk membuat nanokomposit Fe3O4/rGO adalah green synthesis menggunakan ekstrak Moringa oleifera (MO) dan Amaranthus viridis (AV). Karakterisasi hasil penelitian dilakukan menggunakan X-Ray Diffractometer (XRD), Vibrating Sample Magnetometer (VSM), dan Spektrofotometer UV-Visible (UV-Vis). Hasil dari karakterisasi XRD menunjukkan bahwa nanokomposit Fe3O4/rGO memiliki struktur kristal cubic inverse spinel dengan ukuran kristalit 8,83 ± 1,30 nm dan parameter kisinya 7,90 ± 1,43 Å. Sifat magnetik material berdasarkan karakterisasi VSM adalah mendekati superparamagnetik dengan magnetisasi saturasi 21,7 emu/g. Dari hasil analisis UV-VIS diketahui bahwa nanokomposit Fe3O4/rGO memiliki panjang gelombang serapan 308-343 nm dengan energi celah pita sebesar 2,454 ± 0,010 eV. Melalui uji fotokatalitik diperoleh hasil degradasi limbah RhB paling maksimal pada massa 0,07 g dengan waktu penyinaran 180 menit dengan degradasi 98,2%.

In this research, the green synthesis process was successfully carried out and the crystal structure, magnetic properties, and absorption rate of Fe3O4/rGO nanocomposites were known, as well as the effect of catalyst mass on the degradation of rhodamine b waste. The method used to make Fe3O4/rGO nanocomposite is green synthesis using Moringa Oleifera (MO) and Amaranthus Viridis (AV) extracts. Characterization of the results was carried out using X-Ray Diffractometer (XRD), Vibrating Sample Magnetometer (VSM), and UV-Visible Spectrophotometer (UV-Vis). The results of XRD characterization show that the Fe3O4/rGO nanocomposite has a cubic inverse spinel crystal structure with a crystallite size of 8,83 ± 1,30 nm and a lattice parameter of 7,90 ± 1,43 Å. The magnetic properties of the material based on VSM characterization are close to superparamagnetic with a saturation magnetization of 21.7 emu/g. UV-VIS analysis showed that Fe3O4/rGO nanocomposite has an absorption wavelength of 308-343 nm with a band gap energy of 2,454 ± 0,010 eV. Through photocatalytic tests, the maximum degradation of RhB waste was obtained at a mass of 0.07 g with an irradiation time of 180 minutes with 98.2?gradation.

Kata Kunci : fotokatalis, Fe3O4/rGO, green synthesis, rhodamine b (RhB)