Pengaruh Konsentrasi Seng Oksida Nanopartikel (ZnO-NPs) dalam Resin Akrilik Polimerisasi Panas terhadap Kekuatan Fleksural

Ahmad Kholilurrahman, Dr. drg. Dyah Irnawati, MS; Prof. Dr. drg. Widjijono, SU.

2025 | Skripsi | PENDIDIKAN DOKTER GIGI

Resin akrilik polimerisasi panas banyak digunakan sebagai basis gigi
tiruan. Bahan basis gigi tiruan idealnya memiliki kekuatan fleksural yang baik dan
sifat antibakteri. Seng oksida nanopartikel (ZnO-NPs) digunakan sebagai filler
pada resin akrilik karena memiliki sifat antibakteri. Konsentrasi filler
mempengaruhi sifat mekanis resin akrilik. Tujuan penelitian adalah mengetahui
pengaruh konsentrasi ZnO-NPs terhadap kekuatan fleksural resin akrilik.

Penelitian dilakukan menggunakan resin akrilik polimerisasi panas
(Vertex) dan ZnO-NPs dengan ukuran < 100>
berbentuk plat (65 x 10 x 2,5 mm) terdiri dari empat kelompok (n=6) dengan
konsentrasi ZnO-NPs : 0%, 2,5%, 5%, dan 7,5%. Serbuk resin akrilik dan serbuk
ZnO-NPs dicampur sesuai rasio yang sudah ditetapkan menggunakan
amalgamator sampai homogen, kemudian dicampur dengan cairan resin akrilik
dan diproses. Sampel direndam dalam akuades selama 48 jam dan selanjutnya
dilakukan uji kekuatan fleksural dengan universal testing machine. Data kekuatan
fleksural (MPa) dilakukan analisis menggunakan uji ANAVA satu jalur dan uji
LSD0,05.

Hasil penelitian menunjukkan nilai rerata dan standar deviasi kekuatan
fleksural (MPa) kelompok 0%-7,5% secara berurutan: 83,23 ± 6,01; 51,49 ± 5,45;
43,33 ± 3,38; 40,46 ± 2,87. Hasil uji ANAVA satu jalur menunjukkan bahwa
konsentrasi ZnO-NPs memengaruhi kekuatan fleksural resin akrilik secara
signifikan (p<0>LSD0,05 menunjukkan bahwa terdapat perbedaan
kekuatan fleksural resin akrilik yang signifikan antar semua kelompok kecuali
pada kelompok III dan IV. Kesimpulan penelitian ini adalah konsentrasi ZnO-NPs
berpengaruh menurunkan kekuatan fleksural resin akrilik polimerisasi panas.

Heat-polymerized acrylic resin is widely used as a denture base material.
Denture base material should possess good flexural strength and antibacterial
properties. Zinc oxide nanoparticles (ZnO-NPs) are used as a filler in acrylic
resin due to their antibacterial properties. Filler concentration affects the
mechanical properties of acrylic resin. The aim of this study was to investigate the
effect of ZnO-NPs concentration on the flexural strength of acrylic resin.

The study used heat-polymerized acrylic resin (Vertex) and ZnO-NPs with
sizes < 100>
mm) and divided into four groups (n=6) with ZnO-NPs concentrations: 0%, 2.5%,
5%, and 7.5%. The acrylic resin and ZnO-NPs powder were mixed in
predetermined ratio using amalgamator until homogenous, then mixed with
acrylic resin liquid and processed. The samples were soaked in distilled water for
48 hours and flexural strength was tested using universal testing machine.
Flexural strength data (MPa) were analyzed using one-way ANOVA and LSD0.05
test.

The results showed the mean and standard deviation of flexural strength
(MPa) for the 0%-7.5% groups respectively: 83.23 ± 6.01; 51.49 ± 5.45; 43.33 ±
3.38; 40.46 ± 2.87. One-way ANOVA result indicated that ZnO-NPs
concentration significantly affected the flexural strength of acrylic resin (p<0>
LSD0.05 test result showed significant differences in flexural strength among all
groups except groups III and IV. The study concluded that ZnO-NPs
concentration affects decreasing the flexural strength of heat-polymerized acrylic
resin.

Kata Kunci : resin akrilik polimerisasi panas, ZnO-NPs, kekuatan fleksural