EKSPRESI TRANSFORMING GROWTH FACTOR-?1 DAN JUMLAH ODONTOBLAST-LIKE CELL SETELAH APLIKASI KOMPOSIT GELATIN-KITOSAN-TEOS-Ca(OH)2 ATAU Ca(OH)2
Endytiastuti, Dr.drg.Retno Ardhani, M.Sc ; Prof.Dr.drg.Iwa Sutardjo RS.,SU.,Sp.KGA (K)
2024 | Tesis | S2 Ilmu Kedokteran Gigi Klinik
Kalsium hidroksida adalah gold standard
perawatan direct pulp capping, tetapi memiliki kelemahan seperti
menyebabkan tunnel defect dan resorbsi internal gigi sulung. Material komposit pada
penelitian merupakan matriks polimer organik alami (gelatin dan kitosan) yang
berikatan dengan mineral anorganik Ca(OH)2 melalui TEOS sebagai
crosslinker. Penelitian ini bertujuan untuk mengetahui perbedaan respon
pulpa gigi setelah aplikasi Komposit Gelatin-Kitosan-TEOS-Ca(OH)2 dan
Ca(OH)2 pada fase regenerasi.
Penelitian pada model direct
pulp capping gigi molar 1 rahang atas tikus wistar. Preparasi dilakukan
pada bagian oklusal gigi molar pertama rahang atas dengan diamond round bur
no 10 sampai atap kamar pulpa terbuka. Bahan Ca(OH)2 dan
Komposit G/CH/TEOS/Ca(OH)2 diaplikasikan menggunakan aplikator di
atas pulpa yang terbuka pada gigi tikus wistar kemudian tumpatan sementara
digunakan untuk menutup kavitas. Terminasi dilakukan pada 16 ekor tikus di hari
ke-7 dan ke-14 kemudian dilakukan pembuatan blok parafin pada spesimen dan
pewarnaan imunohistokimia untuk mengamati ekspresi TGF-?1 dan pewarnaan
hematoksillin eosin untuk mengamati jumlah odontoblast-like cell.
Pengamatan menggunakan mikroskop cahaya dengan bantuan OptiLab. Analisis
statistik menggunakan uji Kruskal-Wallis dilanjutkan dengan uji Mann-Whitney
pada ekspresi TGF-?1, dan Two-Way ANOVA dilanjutkan uji LSD untuk
mengamati odontoblast-like cell. Penelitian ini menggunakan tingkat
kepercayaan sebesar 95%.
Hasil penelitian menunjukkan terdapat
perbedaan signifikan ekspresi TGF-?1 di hari ke-7 dan ke-14 di antara bahan
kalsium hidroksida dengan G/CH/TEOS/Ca(OH)2 (p=0,01), sedangkan
untuk odontoblast-like cell terdapat perbedaan signifikan jumlah odontoblast-like
cell yang dihasilkan di antara bahan Ca(OH)2 dan G/CH/TEOS/Ca(OH)2
di hari ke-7 dan hari ke-14 (p=0,008). G/CH/TEOS/Ca(OH)2 memiliki
potensi untuk menjadi bahan alternatif selain Ca(OH)2 pada perawatan
direct pulp capping.
Calcium hydroxide is the gold standard treatment for direct pulp capping, but it has weaknesses such as causing tunnel defects and internal resorption of primary teeth. The composite material in this study consists of an organic polymer matrix (gelatin and chitosan) bonded with inorganic smineral Ca(OH)2 through TEOS as a crosslinker. This study aims to determine the difference in dental pulp response after the application of Gelatin-Chitosan-TEOS-Ca(OH)2 composite and Ca(OH)2 in the regeneration phase.
This study is used direct pulp capping model of the maxillary first molar in Wistar rats Preparations were made on the occlusal part of the upper first molar with a round diamond bur no.10 until the pulp chamber roof was exposed. Ca(OH)2 and G/CH/TEOS/Ca(OH)2 were applied using an applicator onto the exposed pulp of Wistar rat teeth, then temporary fillings were used to cover the cavities. Termination was carried out on 16 rats on the 7th and 14th days, then paraffin blocks were made from the specimens and immunohistochemical staining was performed to observe TGF-?1 expression, and hematoxylin-eosin staining was performed to observe the number of odontoblast-like cells. Observation was conducted using a light microscope with the assistance of OptiLab. Statistical analysis was performed using Kruskal-Wallis test followed by Mann-Whitney test for TGF-?1 expression, and Two-Way ANOVA followed by LSD test to observe odontoblast-like cells. This study used a confidence level of 95%.
The results showed a significant difference in TGF-?1 expression on days 7 and 14 between calcium hydroxide and G/CH/TEOS/Ca(OH)2 materials (p=0.01), while for odontoblast-like cells, there was a significant difference in the number of odontoblast-like cells produced between Ca(OH)2 and G/CH/TEOS/Ca(OH)2 materials on days 7 and 14 (p=0.008). G/CH/TEOS/Ca(OH)2 has the potential to be an alternative material for direct pulp capping treatment alongside Ca(OH)2.
Kata Kunci : Ca(OH)2, Ekspresi TGF-?1, G/CH/TEOS/Ca(OH)2, Odontoblast-like cell