Aktivitas Fotokatalitik Green-synthesized Nanokomposit Fe3O4/rGO/TiO2 Menggunakan Ekstrak Moringa Oleifera dan Amaranthus Viridis Untuk Degradasi Zat Pewarna Methylene Blue

HANIF YOMA KHOIRI, Prof. Dr. Eng. Edi Suharyadi, M. Eng.

2023 | Skripsi | FISIKA

Aktivitas fotokatalitik menggunakan green-synthesized nanokomposit Fe3O4/rGO/TiO2 untuk degradasi zat pewarna methylene blue telah berhasil dilakukan. Nanokomposit Fe3O4/rGO/TiO2 disintesis menggunakan pendekatan green-synthesis dengan memanfaatkan ekstrak daun Moringa oleifera dan Amaranthus viridis. Hasil karaktersasi menggunakan X-Ray Diffraction menunjukkan struktur cubic inverse spinel dengan ukuran kristalit sebesar 12,0 ± 0,1 nm. Hasil karakterisasi menggunakan Fourier Transform Infrared menghasilkan serapan pada bilangan gelombang khas Fe3O4/rGO/TiO2. Karakterisasi menggunakan UV-Vis Spectroscopy menunjukkan nanokomposit Fe3O4/rGO/TiO2 memiliki energi celah pita sebesar 3,35 eV. Aktivitas fotokatalitik diamati dengan beberapa variasi konsentrasi fotokatalis. Diperoleh bahwa efisiensi degradasi akan meningkat seiring dengan penambahan konsentrasi fotokatalis. Efisiensi degradasi tertinggi diperoleh sebesar 98?ngan menggunakan 0,0018 g/mL nanokomposit Fe3O4/rGO/TiO2.

Photocatalytic activity of green-synthesized Fe3O4/rGO/TiO2 nanocomposite for degrading methylene blue dye has been successfully carried out. Fe3O4/rGO/TiO2 nanocomposite was synthesized using green-synthesis utilizing Moringa oleifera and Amaranthus viridis leaf extract. The result of characterization using X-Ray Diffraction  showed the spinel inverse cubic structure with crystallite size of 12,0 ± 0,1 nm. The result of characterization using Fourier Transform Infrared showed absorption at typical Fe3O4/rGO/TiO2 wavenumbers. The result of characterization using UV-Vis Spectroscopy showed nanocomposite has 3,35 eV bandgap energy. Photocatalytic activity was carried out with several concentration variations of photocatalyst. The result showed that the degradation efficiency would increase with the increase in photocatalyst concentration. The highest degradation efficiency was obtained at 98% using 0,0018 g/mL of Fe3O4/rGO/TiO2 nanocomposite.

Kata Kunci : fotokatalitik, green-synthesized, Fe3O4/rGO/TiO2, methylene blue

  1. S1-2023-459204-abstract.pdf  
  2. S1-2023-459204-bibliography.pdf  
  3. S1-2023-459204-tableofcontent.pdf  
  4. S1-2023-459204-title.pdf  
  5. S1-2024-459204-abstract.pdf  
  6. S1-2024-459204-bibliography.pdf  
  7. S1-2024-459204-tableofcontent.pdf  
  8. S1-2024-459204-title.pdf