Pengaruh Fraksi Volumetrik Pita Serat Sutra Samia ricini terhadap Kekuatan Tarik Material Fiber Reinforced Composite

ELISSA, Prof. Dr.drg.Siti Sunarintyas, MKes.; Prof. Dr. drg. Widowati Siswomihardjo, M.S.

2023 | Skripsi | PENDIDIKAN DOKTER GIGI

Fiber reinforced composite (FRC) merupakan salah satu material splinting yang bersifat estetik, tersusun atas matriks resin dan fiber. Fiber yang digunakan adalah serat sutra Samia ricini. Tujuan penelitian ini adalah untuk mengetahui pengaruh fraksi volumetrik pita serat sutra Samia ricini terhadap kekuatan tarik material FRC.

Bahan utama yang digunakan adalah resin komposit flowable (Denfil Flow, Korea) dan pita serat Samia ricini. Penelitian ini terdiri dari tiga kelompok, yaitu kelompok I tanpa pita fiber (0%), kelompok II 1 lembar pita fiber (25%), dan kelompok III 2 lembar pita fiber (50%). Setiap kelompok terdiri dari 6 sampel berbentuk dumbbell (30 x 5 x 2) mm. Sampel diuji tarik menggunakan alat Universal Testing Machine. Data dianalisis dengan One way ANOVA dengan taraf signifikansi 0,05.

Hasil pengukuran kekuatan tarik menunjukkan rerata kelompok I (59,95 ± 4,47 MPa), kelompok II (37,78 ± 4,75 MPa), dan kelompok III (42,72 ± 5,34 MPa). Hasil uji One way ANOVA menunjukkan terdapat pengaruh fraksi volumetrik pita serat Samia ricini terhadap kekuatan tarik material FRC (p kurang dari 0,05). Hasil uji Post Hoc LSD menunjukkan perbedaan bermakna pada kelompok I dan II, serta kelompok I dan III. Kesimpulan penelitian ini adalah terdapat pengaruh penambahan pita serat sutra Samia ricini terhadap kekuatan tarik material FRC.

Fiber reinforced composite (FRC) is one of the aesthetic splinting materials, composed of a matrix resin and fiber. The fiber used was Samia ricini silk fiber. The purpose of this study was to determine the effect of volumetric fraction of Samia ricini silk fiber band on the tensile strength of FRC material.

The main ingredients used were flowable composite resin (Denfil Flow, Korea) and Samia ricini fiber band. This study consisted of three groups, namely group I without fiber band (0%), group II 1 sheet of fiber band (25%), and group III 2 sheets of fiber band (50%). Each group consists of 6 dumbbell-shaped samples (30 x 5 x 2) mm. The sample is tensile tested with a Universal Testing Machine. The data was analyzed with One-way ANOVA with significance level of 0.05.

The result of tensile strength measurements showed the average of group I (59.95 ± 4.47 MPa), group II (37.78 ± 4.75 MPa), and group III (42.72 ± 5.34 MPa). The results of the One-way ANOVA test show that there is an effect of the volumetric fraction of Samia ricini fiber band on the tensile strength of FRC material (p less than 0.05). Post Hoc LSD test results show significant differences in groups I and II, and groups I and III. The conclusion of this study is that there is an effect of the addition of Samia ricini silk fiber bands on the tensile strength of FRC materials.

Kata Kunci : fiber reinforced composite, Samia ricini, fraksi volume, kekuatan tarik

  1. S1-2023-458961-abstract.pdf  
  2. S1-2023-458961-bibliography.pdf  
  3. S1-2023-458961-tableofcontent.pdf  
  4. S1-2023-458961-title.pdf  
  5. S1-2024-458961-abstract.pdf  
  6. S1-2024-458961-bibliography.pdf  
  7. S1-2024-458961-tableofcontent.pdf  
  8. S1-2024-458961-title.pdf