Kajian Pengaruh Konsentrasi Dopan Ion Sr2+ Terhadap Sifat Fisikokimia Material HA-Ag+ Berbasis Cangkang Lobster Panulirus Homarus

Anisa Nurragita Dewi, Prof. Dr.Eng Yusril Yusuf, S.Si., M.Eng.

2023 | Skripsi | FISIKA

Pada penelitian ini telah berhasil dilakukan kajian penelitian tentang pengaruh variasi konsentrasi dopan ion Sr2+ 1%; 2,5%; dan 5% terhadap sifat fisikokimia pada material HA yang terdoping ion Ag+ berbahan dasar cangkang lobster Panulirus Homarus. Ion Ag+ dan Sr2+ dipilih karena berpotensi memiliki sifat antibakteri dan biokompatibilitas yang baik guna aplikasi pelapis implan gigi. Penelitian ini bertujuan untuk mengetahui konsentrasi terbaik dari ion Sr2+ pada material HA-Ag+ melalui parameter-parameter fisikokimia. Hasil yang didapatkan dapat dijadikan sebagai informasi dan referensi bagi penelitian selanjutnya pada kajian biomaterial hidroksiapatit. Perlakuan doping ion dilakukan menggunakan metode hidrotermal pada suhu 200°C selama 8 jam. Metode karakterisasi material dilakukan dengan XRD, FTIR, dan SEM-EDX. Hasil pengaruh penambahan konsentrasi doping ion Sr2+ pada sampel HA-Ag+ menyebabkan penurunan ukuran kristal (45±1) nm dan penambahan nilai microstrain (0,0032). FTIR mengonfirmasi adanya gugus fungsi OH-, CO32-, PO42-, dan HPO42-. Ukuran mikropori (0,80±0,03) µm, persentase porositas (74,54%), jumlah persentase massa (1,30%), dan rasio Ca/P (1,65) juga meningkat sejalan dengan penambahan konsentrasi doping ion Sr2+. Adapun untuk konsentrasi terbaik dari doping ion adalah 5% sebagai kandidat material pelapis pada implan gigi.

This study has successfully conducted a research study on the effect of variations in Sr2+ ion dopant concentrations of 1%; 2.5%; and 5% on the physicochemical properties of Ag+ ion-doped HA material based on Panulirus Homarus lobster shells. Ag+ and Sr2+ ions were chosen because they potentially have good antibacterial and biocompatibility properties for dental implant coating applications. This study aims to determine the best concentration of Sr2+ ions in HA-Ag+ material through physicochemical parameters. The results obtained can be used as information and a reference for further research on hydroxyapatite biomaterial studies. Ion doping treatment was carried out using the hydrothermal method at 200°C for 8 hours. Material characterization methods were carried out by XRD, FTIR, and SEM-EDX. The results of the effect of adding Sr2+ ion doping concentration to the HA-Ag+ sample caused a decrease in crystal size (45 ± 1) nm and an increase in microstrain value (0.0032). FTIR confirmed the presence of functional groups of OH-, CO32-, PO42-, dan HPO42-. Micropore size (0.80±0.03) µm, porosity percentage (74.54%), total mass percentage (1.30%), and Ca/P ratio (1.65) also increased in line with the addition of Sr2+ ion doping concentration. The best concentration of ion doping is 5% as a candidate for coating material in dental implants.

Kata Kunci : Hidroksiapatit, ion Ag+, ion Sr2+, fisikokimia

  1. S1-2023-442396-abstract.pdf  
  2. S1-2023-442396-bibliography.pdf  
  3. S1-2023-442396-tableofcontent.pdf  
  4. S1-2023-442396-title.pdf