Analisis Sifat Mekanik dan Struktur Mikro pada Pembuatan Panci Susu dengan Metode Metal Spinning

SEPTI PUTRI PRIMA S, Dr. Benidiktus Tulung Prayoga, S.T., M.T.

2022 | Tugas Akhir | D4 TEKNOLOGI REKAYASA MESIN

Metal spinning merupakan salah satu proses pembentukan logam, pada proses pengerjaannya mudah terjadi cacat produk, pemilihan material memudahkan efisiensi produksi. Material yang digunakan yaitu AA1100, ketebalan 1 mm, 2mm. Tujuan penelitian untuk mengetahui pengaruh proses metal spinning berdasarkan hasil uji tarik, uji komposisi kimia, uji struktur mikro dan uji distribusi ketebalan. Metode penelitian menggunakan metode kuantitatif dengan pendekatan penelitian eksperimental. Metode pengumpulan data dengan melakukan observasi, studi literatur, wawancara, dan uji spesimen. Berdasarkan hasil penelitian, uji kekuatan tarik rata-rata ketebalan 1 mm adalah 69,76 MPa dan kekuatan tarik rata-rata ketebalan 2 mm adalah 72,38 MPa, nilai gaya pembentukan rata-rata ketebalan 1 mm adalah 115,53 N, gaya pembentukan rata-rata ketebalan 2 mm adalah 151,63 N. Pengamatan struktur mikro menunjukan ukuran butir mengalami sedikit perubahan, bentuk butir menjadi lebih halus setelah dilakukan pengerjaan spinning. Pengujian distribusi ketebalan menunjukan bahwa ketebalan yang baik digunakan untuk proses spinning adalah ketebalan 2 mm.

Metal spinning is one of the metal forming processes, in the process, it is easy defects in products. In order to avoid it, material selection is being chosen in production efficiency. In this study, aluminum alloy of 1100 with a thickness of 1 mm and 2 mm is used. The aim of this study is to determine the effects of the metal spinning process based on the results of chemical composition tests, observations of microstructure tests, tensile tests and the thickness of the final plate. The research method used was a quantitative method with an experimental research approach. Data collection methods were carried out by conducting observations, literature studies, interviews, and specimen tests. Based on the results, the average tensile strength test at a thickness of 1 mm is 69,76 MPa and the average tensile strength at a thickness of 2 mm is 72,38 MPa, and the value of the average forming force at a thickness of 1 mm is 115,53 N and the average forming force at a thickness of 2 mm is 151,63 N. Microstructure observation shows that the grain size has slightly changed, the grain shape becomes slightly smoother after spinning. The thickness distribution test shows that the best thickness used in the spinning process is a thickness of 2 mm.

Kata Kunci : metal spinning, aluminium paduan, aluminium alloys

  1. D4-2022-460894-tableofcontent.pdf