SINTESIS PET-CDs/BaTiO3 SEBAGAI FOTOKATALIS DEGRADASI METILEN BIRU

RAINDA DEVA S, Prof. Dr. Bambang Rusdiarso DEA.; Prof. Indriana Kartini, M.Si., Ph.D.

2022 | Skripsi | S1 KIMIA

Sintesis fotokatalis PET-CDs/BaTiO3 dan fotodegradasi metilen biru telah dilakukan. Penelitian ini memiliki tujuan untuk membuat karbon dot dari limbah plastik polietilena tereftalat (PET) sebagai komposit fotokatalis dalam medium air dengan bantuan barium titanat (BaTiO3). Sintesis PET-CDs/BaTiO3 dilakukan dalam dua tahap yaitu, (1) sintesis PET-CDs berbahan dasar limbah plastik dengan cara hidrotermal dan (2) pelapisan BaTiO3 dengan PET-CDs menggunakan metode sol-gel. Fotokatalis PET-CDs/BaTiO3 hasil sintesis dikarakterisasi dengan instrumen spektrofotometer UV-Vis, spectrofluorometer, SR UV-Vis spektrofotometer, FT-IR, XRD dan HR-TEM. Uji aktivitas fotokatalitik untuk degradasi metilen biru dilakukan menggunakan paparan cahaya ultraviolet dan cahaya tampak. Fotokatalis PET-CDs/BaTiO3 yang telah disintesis memiliki bentuk serbuk yang tidak larut dalam air dengan ukuran rata-rata 2,88 nm, berfluoresensi biru pada cahaya UV dan memiliki energi celah pita 2,7 eV. Fotokatalis PET-CDs/BaTiO3 yang disintesis memiliki aktivitas fotokatalitik pada cahaya ultraviolet. Kondisi optimum untuk fotokatalitik adalah iradiasi cahaya ultraviolet selama 90 menit menggunakan 30 mg PET-CDs/BaTiO3 dengan 25 mL metilen biru yang mempunyai konsentrasi 10 ppm dengan efisiensi sebesar 32,74%.

Synthesis of PET-CDs/BaTiO3 photocatalyst and methylene blue photodegradation has been carried out. This research aims to make carbon dot compounds from polyethylene terephthalate (PET) plastic waste that can be used as photocatalysts in aqueous solution with the help of barium titanat (BaTiO3). The synthesis of PET-CDs/BaTiO3 had been carried out in two stages namely, (1) the synthesis of PET-CDs with PET plastic waste as base material by hydrothermal method and (2) BaTiO3 coating on PET-CDs by sol-gel method. The synthesized PET-CDs/BaTiO3 photocatalyst was characterized by UV-Vis spectrophotometer, spectrofluorometer, SR UV-Vis spectrophotometer, FT-IR, XRD and HR-TEM instruments. The photocatalytic activity was then tested to degrade methylene blue under ultraviolet and visible light irradiation. The synthesized PET-CDs/BaTiO3 photocatalyst is a powder that is insoluble in water with an average size of 2.88 nm, emitting blue fluorescence in UV light and has a energi celah pita of 3.08 eV. The prepared PET-CDs/BaTiO3 photocatalyst has photocatalytic activity in ultraviolet light. The optimum condition of photocatalytic was obtained at irradiation time for 90 minutes with 30 mg of PET-CDs/BaTiO3 using 25 mL of 10 ppm methylene blue with efficiency of 32.74% under ultraviolet light.

Kata Kunci : Barium titanat, Fotokatalis, Karbon dot, Metilen biru, PET.