SINTESIS SELULOSA SUKSINAT DARI SERAT BAMBU MELALUI REAKSI ESTERIFIKASI DAN APLIKASINYA SEBAGAI ADSORBEN LOGAM BERAT PADA MINYAK BUMI

REMI YULINAR, Prof. Drs. Jumina, Ph.D.; Prof. Dr.rer.nat Harno Dwi Pranowo, M.Si.

2022 | Skripsi | S1 KIMIA

Telah dilakukan sintesis selulosa suksinat dari serat bambu melalui reaksi esterifikasi dan kajian aplikasinya sebagai adsorben logam berat pada minyak bumi. Penelitian ini bertujuan untuk melakukan isolasi alfa-selulosa dari serat bambu dan mensintesis selulosa suksinat menggunakan asam suksinat melalui reaksi esterifikasi. Selain itu, penelitian ini juga bertujuan untuk membandingkan aktivitas alfa-selulosa dengan selulosa suksinat sebagai adsorben logam berat pada sampel minyak bumi. Penelitian ini diawali dengan delignifikasi serat bambu menggunakan natrium hidroksida melalui proses refluks yang diikuti dengan proses isolasi alfa-selulosa. Material alfa-selulosa dimodifikasi dengan asam suksinat melalui reaksi esterifikasi. Material alfa-selulosa dan selulosa suksinat dianalisis dengan spektrofotometer FT-IR dan SEM-EDX. Material alfa-selulosa dan selulosa suksinat digunakan sebagai adsorben logam berat yang terkandung dalam minyak bumi umpan RFCC. Rendemen hasil sintesis selulosa suksinat dengan rasio massa 1 dan 5 kali dari massa alfa-selulosa berturut-turut adalah 82,5% dan 84,0%. Material Alfa-selulosa, selulosa suksinat 1:1, dan selulosa suksinat 1:5 digunakan sebagai adsorben untuk adsorpsi logam Ni(II), Fe(III), dan VO(II) dalam sampel minyak bumi umpan RFCC. Hasil adsorpsi logam Ni(II), Fe(III), dan VO(II) dengan adsorben alfa-selulosa dan selulosa suksinat mengalami fluktuasi pada setiap massa adsorben terhadap logam berat dalam minyak bumi. Hubungan antara massa adsorben dengan kapasitas adsorpsi adalah berbanding terbalik, sedangkan massa adsorben dengan persentase adsorpsi berbanding lurus.

Synthesis of cellulose succinate from bamboo fiber through esterification reaction and its application as an adsorbent for heavy metals in heavy oils have been carried out. This research aimed to isolate alpha-cellulose from bamboo fibers and synthesize cellulose succinate using succinic acid through an esterification reaction. In addition, this study also aims to compare the activity of alpha-cellulose and cellulose succinate as an adsorbent for heavy metals in heavy oil samples. This research was began with the delignification of bamboo fiber using sodium hydroxide through a reflux process and then followed by the isolation process of alpha-cellulose. The alpha-cellulose material was modified with succinic acid through an esterification reaction. The alpha-cellulose and cellulose succinate were analyzed by FTIR spectrophotometer and SEM-EDX. The alpha-cellulose and cellulose succinate were used as adsorbents for heavy metals contained in heavy oil from the RFCC unit. The yield of synthesized cellulose succinate with a mass ratio of 1 and 5 times the mass of alpha-cellulose was 82.5% and 84.0%, respectively. The alpha-cellulose, 1:1 cellulose succinate, and 1:5 cellulose succinate materials were used as adsorbents for the adsorption of Ni(II), Fe(III), and VO(II) metals in the RFCC feed oil. The results of the adsorption of Ni(II), Fe(III), and VO(II) metals with alpha-cellulose and cellulose succinate adsorbents fluctuated at each mass of the adsorbent against heavy metals in RFCC feed oil. The relationship between the mass of the adsorbent and the adsorption capacity is inversely proportional, while the mass of the adsorbent and the adsorption percentage is directly proportional.

Kata Kunci : adsorpsi, esterifikasi, minyak bumi, selulosa suksinat, serat bambu/ adsorption, bamboo fiber, cellulose succinate, crude oil, esterification