PENGARUH PELAPISAN SILVER DAN KONDISI SUHU PADA RONGGA MULUT TERHADAP PELEPASAN ION KOBALT DAN KROMIUM KERANGKA LOGAM GIGI TIRUAN

DIANA OMEGA PAMUDJI, Prof. Dr. drg. Haryo Mustiko D., MS., Sp.Pros(K); drg. Murti Indrastuti, M.Kes., Sp.Pros(K)

2022 | Tesis-Spesialis | PROSTODONSIA

Logam campur kobalt kromium (CoCr) sering digunakan sebagai basis kerangka logam gigi tiruan lepasan. Perubahan kondisi suhu rongga mulut ketika mengkonsumsi makanan dan minuman dapat menyebabkan korosi logam campur CoCr dan melepaskan ion Co dan Cr. Pelapisan permukaan logam dengan silver dapat meningkatkan resistensi terhadap korosi. Tujuan penelitian ini adalah mengkaji pengaruh pelapisan silver dan kondisi suhu pada rongga mulut terhadap pelepasan ion Co dan Cr pada kerangka logam gigi tiruan. Sampel penelitian berupa plat logam campur CoCr (10mm x 10mm x 2mm) sebanyak 24 keping, terbagi menjadi kelompok logam campur CoCr yang dilapis silver 5 �¼m (kelompok perlakuan) dan tanpa pelapis silver (kelompok kontrol). Sampel kemudian direndam dalam saliva buatan bersuhu 37OC, 50OC dan 70OC selama 14 hari. Hasil perendaman sampel kemudian diuji menggunakan atomic absorption spectrometer untuk melihat konsentrasi pelepasan ion Co dan Cr. Hasil penelitian dianalisa menggunakan uji statistik ANAVA dua jalur dan post hoc LSD. Hasil rerata pelepasan ion Co tertinggi terdapat pada kelompok kontrol di suhu 70OC yaitu 0,249�±0,012 ppm dan yang terendah pada kelompok perlakuan di suhu 37OC yaitu 0,148�±0,019 ppm. Rerata pelepasan ion Cr tertinggi ditunjukkan pada kelompok kontrol di suhu 70OC yaitu 21,102�±1,185 ppb dan yang terendah pada kelompok perlakuan di suhu 37OC yaitu 11,032�±1,956 ppb. Uji statistik ANAVA dua jalur menunjukkan pelapisan silver dan suhu berpengaruh terhadap pelepasan ion Co dan Cr (p<0,05). Uji post hoc LSD terhadap pelepasan ion Co dan Cr menunjukkan terdapat perbedaan signifikan antara variasi suhu 37OC, 50OC dan 70OC di kelompok kontrol maupun perlakuan (p<0,05). Kesimpulan pada penelitian ini adalah pelapisan logam campur CoCr dengan silver ketebalan 5 �¼m dapat menurunkan pelepasan ion Co dan Cr sedangkan kondisi suhu dalam rongga mulut 50OC dan 70OC dapat meningkatkan pelepasan ion Co dan Cr.

Cobalt chromium alloy (CoCr) is a material used as the metal framework for removable dentures. Changes in oral temperature when consuming food and drinks cause corrosion of the CoCr alloy and release Co and Cr ions. Coating metal surfaces with silver can increase corrosion resistance. The purpose of this study was to examine the effect of silver plating and temperature conditions in the oral cavity on the release of Co and Cr ions in the denture metal framework. Research sample consisted of 24 pieces of CoCr alloy plate (10mm x 10mm x 2mm), divided into groups of CoCr alloy coated with 5 �µm silver (treatment group) and without silver coating (control group). The samples were then immersed in artificial saliva at 37OC, 50OC and 70OC for 14 days. The immersion results were then tested using an atomic absorption spectrometer to see the concentration of Co and Cr ions that released. The results of the study were analysed using a two-way ANOVA statistical test and post hoc LSD. The highest mean release of Co ion was 0.249�±0.012 ppm in the control group at 70�°C, and the lowest was 0.148�±0.019 ppm in the treatment group at 37�°C. The highest mean release of Cr ions was 21.102�±1.185 ppb and it was shown in the control group at 70�°C, and the lowest was 11.032�±1.956 ppb in the treatment group at 37�°C. Two-way ANOVA statistical test showed that silver plating and temperature affected the release of Co and Cr ions (p<0.05). Post hoc LSD test on the release of Co and Cr ions showed that there was a significant difference between temperature variations of 37OC, 50OC and 70OC in the control and treatment groups (p<0.05). The conclusion of this study is that the CoCr alloy coating with silver thickness of 5 �µm can reduce the release of Co and Cr ions while the temperature conditions in the oral cavity of 50OC and 70OC can increase the release of Co and Cr ions.

Kata Kunci : Logam campur kobalt kromium, pelapis silver, suhu rongga mulut, ion kobalt, ion kromium.