PENGARUH PENGGUNAAN LIMBAH BETON BEKAS SEBAGAI PENGGANTI AGREGAT KASAR TERHADAP KUAT TEKAN DAN PENYERAPAN AIR PADA BETON

FAQIH ASHARI, Edi Kurniadi, S.T., M.T.

2022 | Tugas Akhir | D3 TEKNIK SIPIL

Pemanfaatan limbah beton sering kali hanya digunakan sebagai bahan urugan saja. Oleh karena itu penulis melakukan penelitian tentang pemanfaatan limbah beton bekas sebagai pengganti agregat kasar untuk kemudian ditinjau bagaimana pengaruhnya terhadap kuat tekan dan daya serap airnya Pengujian dilakukan dengan cara membuat benda uji silinder beton dengan ukuran diameter 150 mm dan tinggi 300 mm. Total benda uji 45 buah dengan 5 variasi penggunaan agregat kasar limbah beton yaitu 0%, 5%, 10%, 15%, dan 20% dimana masing-masing variasi terdiri dari 9 benda uji untuk 3 kali masa pengujian. Yaitu ketika beton berumur 7 hari, 14 hari, dan 28 hari. Setiap benda uji diuji kuat tekan dan serapan airnya. Hasil dari penelitian menunjukkan kuat tekan tertinggi beton umur 7, 14, dan 28 hari terjadi pada variasi 5% agregat limbah. Masing-masing dengan nilai 20,685, 27,987, dan 31,129 MPa. Mengalami kenaikan sebesar 3,5%, 31,98%, dan 28.07% dibandingkan dengan beton normal yang nilai kuat tekannya masing-masing bernilai 19,986, 21,205, dan 24,305 MPa. Dari hasil pengujian serapan air diperoleh. nilai serapan air rata-rata tertinggi beton umur 7,14, dan 28 hari terjadi pada beton dengan variasi 20% yaitu 7,10% mengalami kenaikan 45,27% dibandingkan dengan beton normal dengan nilai serap air rata-rata 4,89%

Utilization of concrete waste is often only used as fill material. Therefore, the author conducted research on the use of used concrete waste as a substitute for coarse aggregate and then reviewed how it affects the compressive strength and water absorption capacity. The test is carried out by making a concrete cylinder test object with a diameter of 150 mm and a height of 300 mm. A total of 45 specimens with 5 variations of the use of coarse aggregate of concrete waste, namely 0%, 5%, 10%, 15%, and 20% where each variation consists of 9 specimens for 3 times the test period. That is when the concrete is 7 days, 14 days, and 28 days. Each specimen is tested for compressive strength and water absorption. The results of the study showed that the highest compressive strength of concrete aged 7, 14, and 28 days occurred at a variation of 5% of waste aggregate. Each with a value of 20,685, 27,987, and 31,129 MPa. There was an increase of 3.5%, 31.98%, and 28.07% coMPared to normal concrete whose compressive strength values were respectively 19.986, 21.205, and 24.305 MPa. From the results of the water absorption test obtained. The highest average water absorption value of concrete aged 7.14, and 28 days occurred in concrete with a variation of 20%, namely 7.10%, an increase of 45.27% coMPared to normal concrete with an average water absorption value of 4.89%

Kata Kunci : kuat tekan, serapan air, limbah beton