Potensi Ekstrak Daun Belimbing Wuluh (Averrhoa Blimbi L) Dalam Mencegah Alergi Kawat Ortodonti Stainless Steel

ASRI ANANDA EDLIN, Dr. drg. Cendrawasih A. F., M.Kes, Sp.Ort. (K) ; drg. Yanuarti Retnaningrum, Sp. Ort.

2021 | Skripsi | S1 KEDOKTERAN GIGI

Perawatan ortodonti dalam waktu yang lama berpotensi menimbulkan resiko yang tidak diinginkan seperti reaksi alergi karena pelepasan ion nikel. Daun belimbing wuluh merupakan bahan alami mengandung senyawa tanin yang diketahui bermanfaat sebagai inhibitor korosi kawat ortodonti. Tujuan narrative review ini adalah untuk mengetahui potensi ekstrak daun belimbing wuluh dalam mencegah alergi kawat ortodonti stainless steel dan membahas prosedur - prosedur untuk mengevaluasi alergi dalam perawatan ortodonti. Database yang digunakan untuk mencari literatur dalam karya tulis ini yaitu Pubmed, Science Direct, dan Google Scholar. Pencarian literatur menggunakan kata kunci orthodontic allergy, orthodontic corrosion, metal ion release, stainless steel, biocompatibility test, allergic test, patch test, inhibitor organic, animal, human. Literatur diseleksi menggunakan kriteria inklusi dan eksklusi. Hasil review menunjukkan bahwa ekstrak daun belimbing wuluh mengandung senyawa tanin yang dapat berikatan dengan logam membentuk lapisan pasif. Lapisan pasif tersebut berfungsi sebagai proteksi agar nikel pada kawat ortodonti stainless steel tidak lepas ke rongga mulut sehingga alergi selama perawatan ortodonti dapat dicegah. Beberapa prosedur uji biokompatibilitas yang dibahas dalam review ini dapat digunakan untuk mengevaluasi alergi diantaranya uji sensitisasi guinea pig maximisation test (GPMT), uji implantasi, patch test, dan uji sitotoksisitas MTT assay. Karya tulis ini selanjutnya diharapkan dapat digunakan sebagai acuan penelitian mengenai efektivitas ekstrak daun belimbing wuluh dalam mencegah alergi kawat ortodonti stainless steel. Kata kunci: Orthodontic Allergy, Inhibitor Corrosion, Allergic Test, Averrhoa blimbi L.

Orthodontic treatment in a long period potentially induces negative risk such as allergic reaction caused by nickel ion relase. Wuluh starfuit leaf as a natural ingredient contains tannin that can be use as corrosion inhibitor. This narrative review aims to determine the effect of wuluh starfruit leaf extract to prevent orthodontic allergy by stainless steel wire and to analyze biocompatibility procedures in evaluating orthodontic allergy. The databases used to search the literatures in this review are Pubmed, Science Direct, and Google Scholar. The keywords used in this review are "orthodontic allergy, orthodontic corrosion, metal ion release, stainless steel, biocompatibility test, allergic test, patch test, inhibitor organic, animal, human". The literatures were selected using inclusion and exclusion criteria. The result of this review showed that wuluh starfruit leaf extract contains tannin which can form passive layer on metal surface. The passive layer serves as protection against corrosion so the nickel ions in stainless steel wire do not release to oral cavity and allergic reaction during orthodontic treatment can be prevented. Several biocompatibility tests in this review can be used to evaluate orthodontic allergy: sensitisation test guinea pig maximisation test (GPMT), subcutaneous implantation test, patch test, and cytotoxycity MTT assay test. This narrative review is expected to be used as a reference for research on the effectiveness of wuluh starfruit leaf extract in preventing orthodontic allergy. Keywords: Orthodontic Allergy, Inhibitor Corrosion, Allergic Test, Averrhoa blimbi L.

Kata Kunci : Orthodontic Allergy, Inhibitor Corrosion, Allergic Test, Averrhoa blimbi L