PENGARUH PASTA GIGI PEMUTIH TERHADAP PERUBAHAN WARNA RESIN KOMPOSIT NANOFIL YANG MENGALAMI DISKOLORASI KOPI ROBUSTA

LUISA KANDIDA, Dr. drg. Tunjung Nugraheni, MKes, Sp.KG(K); drg.Wignyo Hadriyanto, M.S, Sp.KG (K)

2020 | Skripsi | S1 KEDOKTERAN GIGI

INTISARI Dewasa ini, pasta gigi pemutih telah banyak digunakan bagi gigi dan restorasi karena efek pembersihan yang didapat dari bahan abrasif dan bahan kimia yang terkandung didalamnya. Resin komposit nanofil merupakan material restorasi yang telah banyak digunakan, namun terdapat kelemahan yaitu perubahan warna akibat adanya penyerapan air kedalam matriks dan bahan pengisi secara difusi. Kopi robusta merupakan salah satu faktor ekstrinsik yang dapat menyebabkan perubahan warna melalui zat warna tanin yang menimbulkan warna kuning kecokelatan. Tujuan penlitian ini ialah mengetahui pengaruh pasta gigi pemutih terhadap perubahan warna resin komposit nanofil yang mengalami diskolorasi kopi robusta. Penelitian dilakukan pada 20 diskus resin komposit nanofil dengan diameter 10 mm dan tebal 2 mm. Spesimen direndam dalam saliva buatan dengan suhu 37oC selama 24 jam dan dilanjut perendaman larutan kopi robusta dengan suhu 50oC-60oC selama 48 jam kemudian diukur nilai awal dengan alat chromameter. Spesimen dibagi menjadi dua kelompok berdasarkan perlakuan penyikatan yakni menggunakan pasta gigi tanpa pemutih (kontrol) dan pasta gigi pemutih. Parameter pengukuran warna menurut sistem L*a*b* diukur menggunakan chromameter sebelum dan setelah perlakuan. Data perubahan warna dihitung kemudian dianalisis dengan uji T tidak berpasangan. Hasil uji T tidak berpasangan menunjukan nilai signifikansi sebesar 0.000 (p<0.05) yang menunjukan bahwa terdapat perbedaan yang signifikan antara kelompok penyikatan dengan pasta gigi pemutih dan tanpa pemutih. Kesimpulan dari penelitian ini adalah terdapat pengaruh pasta gigi pemutih terhadap perubahan warna resin komposit nanofil yang mengalami diskolorasi kopi robusta yang signifikan.

ABSTRACT Nowadays, whitening toothpaste is widely used for teeth and restoration because of the cleansing effect obtained from abrasive materials and chemicals in it. Nanofilled composites resin is a restoration material that has been widely used, but there is a weakness, that is change in color due to the absorption of water into the matrix and filler material by diffusion. Robusta coffee is one of the extrinsic factors that can cause discoloration through tannins which cause a brownish yellow color. The purpose of this study was to determine the effect of whitening toothpaste on nanofilled composite resin color changed due to Robusta coffee discoloration. This research used 20 samples of cylindrical shaped nanofilled composite resin with the diameter of 10 mm and 2 mm thickness. Specimens were immersed in artificial saliva at 37oC for 24 hours and then immersions in Robusta coffee solution at 50oC-60oC for 48 hours then the initial values were measured with a chromameter. The specimens were divided into two groups based on the treatment of brushing is to use non whitening toothpaste (control) and whitening toothpaste. Color measurement parameters according to L*a*b* system using chromameter before and after treatment. The data of color change was calculated and analyzed using independent T test. Independent T test results showed that the significance value was 0.000 (p<0.05) which showed that there was a significant difference between the brushing with non-whitening and whitening toothpaste. The conclusion of this study is that there is an effect of whitening toothpaste on the color changed of nanofilled composite resin due to significant Robusta coffee discoloration.

Kata Kunci : resin komposit nanofil, pasta gigi pemutih, kopi robusta, diskolorasi