PENGARUH pH BASA TERHADAP KEMAMPUAN SWELLING DAN FOTOKATALIS KOMPOSIT PVA/TiO2

Dian Nur Mahardika, Dr. Sc. Ari Dwi Nugraheni, S.Si., M.Si

2019 | Skripsi | S1 FISIKA

INTISARI PENGARUH pH BASA TERHADAP KEMAMPUAN SWELLING DAN FOTOKATALIS KOMPOSIT PVA/TiO2 Oleh Dian Nur Mahardika 15/378009/PA/16484 Membran nanofiber polyvinil alcohol (PVA)/titanium dioksida (TiO2) telah dibuat dengan metode elektrospining. Nanofiber di-crosslink menggunakan gutaraldehyde (GA) untuk menjaga kestabilannya di dalam cairan. Untuk mencegah penggumpalan pada nanopartikel TiO2 dilakukan treatment sonikasi dan penambahan surfaktan tetramethylammonium hydroxide (TMAH). Nanofiber PVA/TiO2 diuji Scanning Electron Microscopy (SEM) untuk mengetahui morfologi dan diameter nanofiber.Uji swelling untuk mengetahui kemampuan swelling nanofiber PVA/TiO2 dengan merendam pada larutan pH yaitu 7, 8, 9, 10, 11, dan 12 dengan waktu tertentu. Selanjutnya diuji fotokatalis untuk mengetahui kemampuan degradasi dari nanofiber PVA/TiO2 dengan melarutkan pH 7, 8, 9, 10, 11, dan 12 dalam larutan methylene blue (MB). Karakterisasi SEM menunjukkan bahwa rata-rata diameter nanofiber PVA/TiO2 sebesar (406± 167) nm. Hasil uji swelling menunjukkan rasio swelling menurun seiring dengan naiknya pH basa. Hasil uji fotokatalis menunjukkan kemampuan fotokatalis semakin meningkat seiring dengan meningkatnya nilai pH basa, namun terjadi anomali pada grafik pH 12. Membran fotokatalis nanofiber PVA/TiO2 mampu mendegradasikan larutan methylene blue hingga 92,2% selama 2 jam pada pH 11. Membran fotokatalis nanofiber PVA/TiO2 juga mempunyai kemampuan dapat digunakan kembali (reusable) untuk fotokatalis.

ABSTRACT EFFECT OF BASIC pH ON SWELLING CAPABILITY AND PHOTOCATALYSIS OF PVA / TiO2 COMPOSITE By Dian Nur Mahardika 15/378009/PA/16484 The polyvinil alcohol (PVA)/titanium dioksida (TiO2) nanofiber membrane was fabricated successfully by electrospinning methods. Glutaraldehyde crosslinking agent was added to increase membrane stability in water. To prevent the agglomeration of TiO2 nanoparticles was done by sonication treatment and tetramethylammonium hydroxide (TMAH) surfactant addition. The PVA/TiO2 nanofiber was investigated by using Scanning Electron Microscopy (SEM) to determine the morphology and the diameter of the nanofiber. Swelling test to determine the swelling ability of PVA/TiO2 nanofiber by soaking in solution of pH 7, 8, 9, 10, 11, and 12 with a certain time. Next, photocatalyst test to determine the degradation ability of PVA / TiO2 nanofiber by dissolving pH 7, 8, 9, 10, 11, and 12 in a solution of methylene blue (MB).The characterization of SEM showed that the average diameters of PVA/TiO2 nanofiber is (406 ± 167) nm. Swelling test indicated that swelling ratio decreases with increasing pH solutions. Photocatalyst test results show the abilities of photocatalyst increases with increasing of base pH, but the anomalies occur on the pH 12 graph. The nanofiber photocatalytic membrane of PVA/TiO2 has dye removal of methylene blue until 92,2% was degraded for 2 hours at pH 11. The PVA/TiO2 nanofiber membrane also reuseable for photocatalysts.

Kata Kunci : PVA, TiO2, swelling, fotokatalis, pH basa