PENGARUH PERBEDAAN TEKNIK MOLDING BASIS GIGI TIRUAN RESIN AKRILIK DENGAN PARTIKEL NANO SILICA COATING 0,5% TERHADAP PERLEKATAN CANDIDA ALBICANS

HARDI PRABOWO, drg. Erwan Sugiatno, M.S., Sp.Pros (K), Ph.D ; drg. Heriyanti Amalia Kusuma, S.U., Sp. Pros (K)

2019 | Tesis-Spesialis | PROSTODONSIA

Basis gigi tiruan resin akrilik dibuat dengan teknik molding konvensional dan injeksi. Partikel nano silica dioxide (SiO2) telah digunakan sebagai bahan coating basis gigi tiruan untuk meningkatkan karakteristik dari resin akrilik. Candida albicans merupakan jamur yang bersifat komensal pada rongga mulut. Tujuan penelitian ini adalah mengkaji pengaruh perbedaan teknik molding dengan partikel nano silica 0,5% coating terhadap perlekatan Candida albicans pada basis gigi tiruan resin akrilik (kajian in vitro). Sampel terdiri dari 24 cakram resin akrilik dengan diameter 5 mm dan tebal 2 mm, dibagi menjadi 4 kelompok (n=6) yaitu kelompok teknik molding konvensional dan injeksi yang diberikan silica coating dan tanpa coating. Seluruh kelompok sampel direndam dalam sediaan saburoud dextrose broth yang berisi Candida albicans dan diinkubasi selama 24 jam pada suhu 370C. Candida albcans yang menempel pada sampel dirontokkan dan dibiakkan pada sediaan saburoud dextrose agar dan dihitung jumlah koloninya (CFU/ml). Analisis statistik dengan Anava dua jalur dilanjutkan uji post hoc LSD (p<0,05). Hasil penelitian menunjukkan nilai rerata perlekatan Candida albicans paling rendah pada kelompok teknik molding injeksi dengan silica coating (350 lebih kurang 187 CFU/ml) dan paling tinggi pada kelompok teknik molding konvensional tanpa silica coating (2033 lebih kurang 266 CFU/ml). Uji Anava dua jalur menunjukkan perbedaan teknik molding dan silica coating berpengaruh terhadap perlekatan Candida albicans. Uji post hoc LSD menunjukkan terdapat perbedaan bermakna perlekatan Candida albicans pada kelompok teknik molding injeksi dengan silica coating dengan seluruh kelompok (p<0,05). Kesimpulan penelitian adalah teknik molding injeksi dan pemberian silica coating pada cakram resin akrilik dapat mengurangi perlekatan Candida albicans.

Acrylic resin denture bases can be made with conventional and injection molding techniques. Nano silica dioxide (SiO2) particles have been used as a denture base coating material to improve the mechanical properties of acrylic resins. Candida albicans is a commensal fungus in the oral cavity. The aim of this study was to examine the effect of differences in molding techniques with 0,5% nano silica coating particles on the attachment of Candida albicans on an acrylic resin denture base (in vitro study). The sample consisted of 24 acrylic resin discs with a diameter of 5 mm and a thickness of 2 mm, divided into 4 groups (n = 6), namely the conventional molding and injection technique group given silica coating and without coating. The entire sample group was immersed in a saboraud dextrose agar preparation containing Candida albicans and incubated for 24 hours at 370C. Candida albicans attached to the sample were broken down and bred on saboroud dextrose broth and the number of colonies (CFU / ml) was calculated. Statistical analysis were done with two-way ANOVA and further tested using post hoc LSD test (p <0.05). The results showed the lowest value of Candida albicans attachment in the injection molding technique group with silica coating (350 about 187 CFU / ml) and the highest in the conventional molding technique group without silica coating (2033 about 266 CFU / ml). Two-way ANOVA Test showed differences in molding and silica coating techniques affect the attachment of Candida albicans. The post hoc LSD test showed that there was a significant difference in the attachment of Candida albicans in the injection molding technique group with silica coating with the whole group (p <0.05). The conclusion of the research is the injection molding technique and the administration of silica coating on acrylic resin discs is able to reduce the attachment of Candida albicans.

Kata Kunci : Canida albicans, resin akrilik, teknik molding, silica coating/acrylic resin, Canida albicans, molding technique, silica coating