SINTESIS HIDROKSIAPATIT DARI CANGKANG TELUR BEBEK SEBAGAI ADSORBEN ION [AuCl4]-

RAYMENDO ESTOMIHI SINAGA, Dr. Sri Sudiono, M.Si.

2019 | Skripsi | S1 KIMIA

Telah dilakukan penelitian sintesis hidroksiapatit dari cangkang telur bebek sebagai adsorben ion [AuCl4]-. Penelitian ini bertujuan untuk melakukan sintesis hidroksiapatit dari cangkang telur bebek, menentukan pH optimum, isoterm dan kinetika adsorpsi [AuCl4]- oleh hidroksiapatit. Sintesis hidroksiapatit diawali dengan melarutkan serbuk cangkang telur bebek 60 mesh dalam larutan HNO3 65 persen kemudian ditambah dengan larutan H3PO4 85 persen serta larutan NH4OH 25 persen hingga pH 10. Cangkang telur hasil sintesis dikeringkan pada temperatur 80 derajat celcius selama 24 jam dilanjutkan dengan kalsinasi pada temperatur 600 derajat celcius selama 3 jam. Penentuan pH optimum adsorpsi [AuCl4]- ditentukan dengan menginteraksikan hidroksiapatit dengan [AuCl4]- pada variasi pH 1 sampai 8. Isoterm adsorpsi [AuCl4]- ditentukan dengan cara menginteraksikan hidroksiapatit dengan larutan [AuCl4]- variasi konsentrasi pada pH optimum. Penentuan kinetika adsorpsi [AuCl4]- dilakukan dengan menginteraksikan hidroksiapatit dengan [AuCl4]- pada pH optimum pada variasi waktu. Filtrat sebelum dan sesudah interaksi antara hidroksiapatit dengan [AuCl4]- dianalisis dengan spektrofotometer UV-Visible. Adsorben sebelum dan sesudah interaksi dengan [AuCl4]- dianalisis dengan menggunakan spektrofotometer FTIR dan difraksi sinar X. Berdasarkan hasil penelitian, adsorpsi [AuCl4]- oleh hidroksiapatit optimum pada pH 3. Adsorpsi [AuCl4]- oleh hidroksiapatit mengikuti model isoterm Langmuir dengan kapasitas adsorpsi maksimum sebesar 9,35 x 10-5 mol per gram dan perubahan energi bebas Gibbs sebesar -27,741 kiloJoule per mol. Kinetika adsorpsi [AuCl4]- pada hidroksiapatit mengikuti model kinetika orde dua semu Ho dengan konstanta laju reaksi sebesar 0,0171 gram per mol menit.

Synthesis of hidroxyapatite from duck eggshell as an adsorbent for [AuCl4]- ion has been done. This research was aimed to synthesize hydroxyapatite from duck eggshell, determine the optimum pH for adsorption [AuCl4]-, evaluate the isotherm adsorption, and determine the kinetics adsorption of [AuCl4]- by hidroxyapatite. Synthesis of hydroxyapatite was started by dissolving duck's eggshell powder 60 mesh in solution of HNO3 65 percent, followed by addition of H3PO4 85 percent then NH4OH 25 percent solution to pH 10. The result of synthesis was dried at 85 degrees celcius then calcined at 600 degrees celcius for 3 hours. The determination of optimum pH was carried out by interacting hydroxyapatite with [AuCl4]- under various pH 1 to 8. The study of isotherm adsorption was carried out by interacting hydroxyapatite and a solution of [AuCl4]- with various concentrations at optimum pH. The kinetics adsorption of [AuCl4]- was investigate by interacting hydroxyapatite with [AuCl4]- at the pH optimum under variation of time. The filtrate before and after interaction between hydroxyapatite and [AuCl4]- were analyzed by UV-Visible spectrophotometer. Adsorbent before and after interaction with [AuCl4]- were analyzed by FTIR spectrophotometer and X-ray diffraction. The results showed that the adsorption of [AuCl4]- by hydroxyapatite optimum at pH 3. The adsorption [AuCl4]- by hydroxyapatite followed Langmuir isotherm model with maximum adsorption capacity 9,35 x 10-5 mole per gram and Gibbs free energy 27,741 kiloJoule per mole. The adsorption kinetics of [AuCl4]- on hydroxyapatite followed pseudo second order Ho model with reaction rate constant 0,0171 gram per mole minutes.

Kata Kunci : hidroksiapatit, [AuCl4]-, isoterm adsorpsi, kinetika adsorpsi