FABRIKASI NANOFIBER TiO2 BERBASIS PREKURSOR TITANIUM TETRAISOPROPOXIDE DENGAN METODE ELEKTROSPINNING

REFFANY CHOIRU R, Dr. Eng. Ahmad Kusumaatmaja, M. Sc.

2019 | Tesis | MAGISTER FISIKA

Nanostruktur TiO2 sangat menarik perhatian untuk diteliti belakangan ini karena aplikasinya yang sangat luas. Pada penelitian ini, nanofiber TiO2 disintesis menggunakan metode elektrospinning. Matriks polimer poly (vinyl alcohol) (PVA) dilarutkan ke dalam aquades yang kemudian menjadi umpan saat proses elektrospinning. Proses elektrospinning menggunakan tegangan 15 kV dan jarak jarum ke kolektor 15 cm. Nanofiber PVA yang dihasilkan kemudian dicelupkan ke dalam larutan yang mengandung titanium tetraisopropoxide (TTIP) dan pelarutnya (etanol dan asam asetat). Nanofiber PVA/TTIP kemudian dikalsinasi pada beberapa variasi suhu untuk membentuk nanofiber TiO2. Nanofiber TiO2 dikarakterisasi menggunakan X-ray diffraction spectroscopy (XRD), scannning electron microscopy-energy dispersive spectrometry (SEM-EDS) dan Fourier transform infrared spectroscopy (FTIR). Hasil karakterisasi dianalisis untuk mengetahui morfologi nanofiber, ikatan yang terbentuk pada nanofiber dan fase titanium dioksida yang dihasilkan. Hasil karakterisasi SEM-EDS menunjukkan nanofiber TiO2 berhasil dibentuk pada suhu 500 oC dengan berbagai pelarut. Fase kristal TiO2 yang dihasilkan ialah fase anatase dan rutile.

TiO2 nanostructure has great attention due to their wide application. In this study, TiO2 nanofibers were synthesized using electrospinning methods. Polyvinyl alcohol (PVA) were mixed with distilled water for electrospinning. Electrospinning process used a high voltage of 15 kV and distance tip to colector 15 cm. Then, nanofiber PVA were immersed in solution containing titanium tetraisopropoxide (TTIP) and solvent (ethanol and acetic acid). PVA/TTIP composites were calcined at various temperature to form TiO2 nanofibers. TiO2 nanofibers were characterized by X-ray diffraction spectroscopy (XRD), scanning electron microscopy-energy dispersive spectrometry (SEM-EDS) and fourier transform infrared spectroscopy (FTIR). Characterization results used to determine nanofiber morphology, bond that formed in nanofiber and titania phase. SEM-EDS result show that TiO2 nanofiber has formed at temperature 500 oC with each solvents. Crystal phase of TiO2 that formed are anatase and rutile.

Kata Kunci : titanium tetraisopropoxide, titanium dioksida, elektrospinning, nanofiber