ADSORPSI Au(III) PADA SELULOSA KULIT KELENGKENG DENGAN DAN TANPA PERLAKUAN ASAM SULFAT

CITRA DEWI INDAH SAVITRI, Mokhammad Fajar Pradipta, S.Si., M.Eng

2019 | Skripsi | S1 KIMIA

Telah dilakukan penelitian adsorpsi Au(III) pada selulosa dari kulit kelengkeng (dimocarpus longan lour) hasil perlakuan dengan asam sulfat dan tanpa asam sulfat. Tujuan penelitian ini untuk mempelajari isoterm adsorpsi Au(III) dan membandingkan kemampuan adsorpsi Au(III) oleh kedua adsorben. Penelitian ini diawali dengan preparasi kulit kelengkeng melalui metode asam sulfat dan tanpa asam sulfat. Adsorben yang sudah terbentuk ditentukan isoterm adsorpsi pada variasi konsentrasi 0, 1, 2, 4, 6, 8 dan 10 mM dalam HCl 0,5 M dan dengan variasi temperatur 28, 40, 50 dan 60 C. Konsentrasi Au(III) dalam proses adsorpsi dianalisis dengan menggunakan AAS. Adsorben selulosa asam sulfat dikarakterisasi dengan FTIR, XRD dan foto mikroskop. Adsorben tanpa asam sulfat kulit kelengkeng dikarakterisasi dengan FTIR dan foto mikroskop. Hasil analisis menggunakan FTIR menunjukkan bahwa adsorben memiliki beberapa gugus fungsional diantaranya O-H, C-O-C, -C=O dan C-H. Karakteristik adsorben selulosa dengan asam sulfat dari kulit kelengkeng dengan XRD menunjukkan sifat amorf dan difraktogram adsorben selulosa dengan asam sulfat dari kulit kelengkeng setelah interaksi dengan Au(III) menunjukkan beberapa puncak karakteristik dengan tipe face centered cubic (fcc). Berdasarkan perhitungan dari hasil penelitian untuk adsorben selulosa dengan asam sulfat dari kulit kelengkeng diperoleh kapasitas adsorpsi maksimum (Qmaks), energi bebas Gibbs, entalpi adsorpsi dan entropi sebesar 3,919 mmol g-1; -23,01 kJ mol-1; 33,02 kJ mol-1 dan 169,3 J mol-1 K-1 dengan model isoterm Langmuir. Adsorben dengan tanpa asam sulfat kulit kelengkeng diperoleh kapasitas adsorpsi maksimum (Qmaks), energi bebas Gibbs, entalpi adsorpsi dan entropi sebesar 1,648 mmol g-1; -24,00 kJ mol-1; 22,39 kJ mol-1 dan 138,1 J mol-1 K-1. Hasil parameter termodinamika membuktikan adsorben selulosa dengan asam sulfat dari kulit kelengkeng lebih baik mengadsorpsi Au(III) daripada tanpa asam sulfat kulit kelengkeng.

Au (III) adsorption studies on cellulose from longan peel (dimocarpus longan lour) have been carried out as a result of treatment with sulfuric acid and without sulfuric acid. The purpose of this study was to study the Au (III) adsorption isotherm and compare the adsorption ability of Au (III) by both adsorbents. This study began with the preparation of longan peel through the method of sulfuric acid and without sulfuric acid. The adsorbent that has been formed is determined by adsorption isotherm at various concentrations of 0, 1, 2, 4, 6, 8 and 10 mM in 0.5 M HCl and with temperature variations of 28, 40, 50 and 60 C. The Au (III) concentration in the adsorption process was analyzed using AAS. Cellulose sulfuric acid adsorbent was characterized by FTIR, XRD and microscope photos. Adsorbents without sulfuric acid kelengkeng peel were characterized by FTIR and microscope photos. The results of the analysis using FTIR showed that the adsorbent had several functional groups including O-H, C-O-C, -C = O and C-H. The characteristics of cellulose adsorbent with sulfuric acid from longan peel with XRD showed amorphous properties and diffractogram of cellulose adsorbent with sulfuric acid from longan peel after interaction with Au (III) showed several characteristic peaks with face centered cubic (fcc) types. Based on calculations from the results of research for cellulose adsorbent with sulfuric acid from kelengkeng peel, the maximum adsorption capacity, Gibbs free energy, enthalpy adsorption and entropy of 3,919 mmol g-1; -23.01 kJ mol-1; 33.02 kJ mol-1 and 169.3 J mol-1 K-1 with the Langmuir isotherm model. Adsorbents with no sulfuric acid of kelengkeng obtained maximum adsorption capacity, Gibbs free energy, enthalpy adsorption and entropy of 1,648 mmol g-1; -24.00 kJ mol-1; 22.39 kJ mol-1 and 138.1 J mol-1 K-1. The results of the thermodynamic parameters prove that cellulose adsorbent with sulfuric acid from longan peel is better to adsorb Au (III) than without sulfuric acid of longan peel.

Kata Kunci : adsorben, adsorpsi Au(III), isoterm adsorpsi dan parameter termodinamika