Perilaku Swelling Pada Membran Fotokatalis Nanofiber Polyvinyl Alcohol (PVA)/ Kitosan/ TiO2

DIKI PURNAWATI, Dr.Sc. Ari Dwi Nugraheni, M.Sc.

2019 | Tesis | MAGISTER FISIKA

Pembuatan membran fotokatalis nanofiber PVA/Kitosan/TiO2 telah berhasil dilakukan dengan metode electrospinning. Membran fotokatalis nanofiber PVA/Kitosan/TiO2 dibuat dengan rasio massa PVA/Kitosan (w/w) 90/10, 85/15, 80/20, dan 70/30. Masing � masing sampel di-crosslink dengan menggunakan Glutaraldehide (GA) untuk menjaga stabilitasnya didalam medium cair. Selanjutnya dilakukan pengujian swelling pada 3 variasi pH untuk mengetahui perilaku swelling dari membran fotokatalis nanofiber PVA/Kitosan/TiO2 . Data hasil penelitian menunjukkan bahwa penambahan konsentrasi Kitosan pada membran fotokatalis nanofiber PVA/Kitosan/TiO2 akan sebanding dengan peningkatan beads, penurunan nilai diameter fiber, penurunan rasio swelling, dan peningkatan nilai waktu konstan (�). Hasil uji fotokatalis menunjukkan bahwa peningkatan rasio swelling sebanding dengan peningkatan kemampuan fotokatalis dari membran fotokatalis nanofiber PVA/Kitosan/TiO2. Membran fotokatalis nanofiber PVA/Kitosan/TiO2 dengan perbandingan rasio massa PVA/Kitosan 90/10 mampu mendegradasi larutan Metilen Biru (MB) sebanyak 97% dalam waktu 2 jam.

Nanofiber photocatalytic membranes of PVA/Chitosan/TiO2 has successfully fabricated using electrospinning method. Nanofiber photocatalytic membranes of PVA/Chitosan/TiO2 was produced with mass ratio PVA/Chitosan (w/w) 90/10, 85/15, 80/20, and 70/30. Glutaraldehyde crosslinking was added to increase membrane stability in water. Swelling behaviour was tested in 3 various pH to investigate the swelling behaviour of nanofiber photocatalytic membranes of PVA/Chitosan/TiO2. The result indicated that the addition of Chitosan concentration will increase number of beads, decrease of fibers diameters, decrease of swelling index, and increase of time constant (�). The photocatalytic result indicated that photocatalyc activity tends to increase due to swelling index increase. Nanofiber photocatalytic membranes of PVA/Chitosan/TiO2 with mass ratio of PVA/Chitosan 90/10 has dye removal of 97% dye was degrade in 2 hours.

Kata Kunci : swelling, membrane, photocatalytic, PVA, Chitosan, TiO2