PENGARUH PENAMBAHAN E-GLASS FIBER NON DENTAL PADA ZONA KOMPRESI TERHADAP KEKUATAN IMPAK BASE PLATE RESIN AKRILIK

MARA GUSTINA, Prof. Dr. Drg. Widjijono SU;Dr. Drg. Endang Wahyuningtyas,M.S.,Sp.Pros(K)

2019 | Tesis | MAGISTER ILMU KEDOKTERAN GIGI

Glass fiber non dental merupakan salah satu bahan yang dapat digunakan untuk meningkatkan kekuatan impak base plate resin akrilik, yang memiliki komposisi yang hampir sama dengan e-glass fiber dental. Orientasi dan posisi fiber berpengaruh terhadap keefektifan untuk penguatan. Penelitian ini bertujuan untuk mengkaji pengaruh orientassi glass fiber non dental pada posisi kompresi terhadap kekuatan impak base plate resin akrilik. Penelitian dilakukan terhadap 16 sampel plat resin akrilik dengan penambahan fiber (65mm x 10 mm x 2,5 mm), yang terbagi dalam 4 kelompok (kombinasi orientasi unidirectional, bidirectional, dan woven pada posisi kompresi). Material yang digunakan dalam penelitian ini adalah resin akrilik heat cured merk QC-20, glass fiber non dental (tanpa merk). Kekuatan impak diuji menggunakan Impact Testing Mechine. Data yang diperoleh dianalisis menggunakan uji ANOVA satu jalur dan LSD, dengan tingkat kepercayaan 95% (p<0,05) Dalam penelitian ini kekuatan impak base plate dengan penambahan fiber meningkat yaitu : 8,54 ± 2,21; 13,21 ± 2,34; 16,81 ± 2,80 kJ/m2 dibandingkan dengan kelompok kontrol 4,98 ± 1,05 kJ/m2. Uji ANOVA satu jalur menunjukkan terdapat pengaruh bermakna (p<0,05) pada variasi orientasi fiber pada posisi kompresi. Kesimpulan penelitian ini adalah penambahan e-glass fiber non dental (komposisi SiO2, diameter 17,12 sampai 20,03 nanomikron) pada zona kompresi meningkatkan kekuatan impak base plate resin akrilik dan fiber unidirectional memberikan peningkatan kekuatan impak base plate resin akrilik paling tinggi

Glass fiber non dental was one of materials that can be used to increase the impact strength of an base plate resin acrylic , containing a similar composition to that of e-glass fiber dental. Orientation and positions of fiber affected the reinforcement effectiveness. This research aimed to examine the effect of glass fiber non dental orientation in the compression position on the impact strength of base plate resin acrylic. The research was conducted on 16 acrylic resin plate samples with fiber (65 mm x 10 mm x 2.5 mm) addition, which was divided into 4 groups (unidirectional, bidirectional, and woven orientation combination in the compression position). The material used in this study is heat cured acrylic resin QC-20 brand, glass fiber non dental (without any brand). Impact strength was tested using Impact testing machine. The data obtained were analyzed using one-way ANOVA test and LSD, with a confidence level of 95% (p<0,05) In this research the base plate impact strength with the addition of fiber increased 8,54 ± 2,21; 13,21 ± 2,34 ; 16,81 ± 2,80 kJ/m2 compared to the control group 4.98± 1,05 kJ/m2). One-way ANOVA test showed a significant effect (p <0.05) on the fiber orientation variations in the compression position. This research concluded that an addition of e-glass fiber non dental (composed of SiO2 52,56-56,88%), diameter 17,12 sampai dengan 20,03 nanomikron) in the compression zone increased the impact strength of the acrylic resin base plate and fiber unidirectional provided the highest increase in the acrylic resin base plate impact strength

Kata Kunci : glass fiber non dental, orientasi fiber, kekuatan impak