FABRIKASI DAN MORFOLOGI DISTRIBUSI TiO2 PADA MEMBRAN NANOFIBER PVA/TiO2/PVA DENGAN PEMODELAN SANDWICH

ANIN NAHTADIYA UMROTUL ULA, Dr. Chotimah, M.Si.;Dr. Eng. Ahmad Kusumaatmaja, M.Sc.

2019 | Skripsi | S1 FISIKA

Produksi membran nanofiber poly vinyl alcohol (PVA)/Titanuim dioksida (TiO2)/poly vinyl alcohol (PVA) dengan pemodelan sandwich dibuat dengan elektrospining PVA 10% v/v sebagai matriks telah berhasil dibuat. Keunggulan nanofiber ini adalah nanopartikel Titanium dioksida (TiO2) tidak ikut terlarut ketika diaplikasikan pada cairan. Pada nanofiber dilakukan stabilisasi menggunakan Glutaraldehyde (GA) untuk menjaga kestabilannya agar tidak terlarut saat diaplikasikan pada cairan. Fabrikasi nanofiber PVA/TiO2/PVA dilakukan dengan variasi penambahan Tetramethylammonium hydroxide (TMAH) sebagai surfactant dengan perbandingan TiO2:TMAH = 10:1. Membran dikarakterisasi menggunakan SEM (Scanning Electron Microscope). Hasil analisa menunjukkan bahwa penambahan TMAH mengurangi terjadinya aglomerasi dan meningkatkan distribusi TiO2 pada membran.

Nanofiber membrane production of Polyvinyl alcohol (PVA)/Titanuim dioxide (TiO2)/Polyvinyl alcohol (PVA) by the sandwich modeling made with the electrospining PVA 10% v/v as the matrix has been successfully created. The advantage of this nanofiber is that the nanoparticles of Titanium dioxide (TiO2) is soluble when applied to the fluid. The nanofiber was applied the stabilization using Glutaraldehyde (GA) to maintain the stability in order that it was not dissolved when applied to the fluid. The nanofiber fabrication PVA/TiO2/PVA was done by varying the addition of Tetramethylammonium hydroxide (TMAH) as the surfactant with a ratio of TiO2:TMAH = 10:1. The membranes were characterized using SEM (Scanning Electron Microscope). The analysis showed that the addition of TMAH reduced the occurrence of agglomeration and improved the distribution of TiO2 in the membrane.

Kata Kunci : Keywords: PVA/TiO2/PVA, TiO2, electrospinning, nanofiber PVA, TMAH