PEMANFAATAN SENYAWA HIDROKSIAPATIT DARI CANGKANG TELUR BEBEK SEBAGAI ADSORBEN ION Ni(II)

NIA LISNA, Dr. Sri Sudiono, S.Si., M.Si.;Prof. Dr. Triyono, S.U.

2018 | Skripsi | S1 KIMIA

Telah dipelajari pemanfaatan hidroksiapatit dari cangkang telur bebek sebagai adsorben ion Ni(II). Tujuan dari penelitian ini adalah menentukan pH optimum adsorpsi, isotermal adsorpsi, dan model kinetika adsorpsi ion Ni(II) oleh hidroksiapatit dari cangkang telur bebek. Sintesis hidroksiapatit dilakukan dengan melarutkan bubuk cangkang telur bebek ke dalam larutan HNO3 65% dan diikuti dengan penambahan larutan H3PO4 85%. Larutan dibuat menjadi pH 10 menggunakan larutan NH4OH 37%. Suspensi didiamkan pada suhu ruang selama 24 jam. Suspensi disaring, dikeringkan, dan dihaluskan menjadi bubuk. Bubuk hidroksiapatit dipanaskan pada temperatur 600 derajat celcius selama 3 jam. Pengaruh pH terhadap adsorpsi ion Ni(II) oleh hidroksiapatit dilakukan pada variasi nilai pH dari rentang 2-7. Isotermal adsorpsi ditentukan menggunakan model Langmuir dan Freundlich dengan memvariasikan konsentrasi awal adsorbat. Model kinetika adsorpsi ditentukan menggunakan model Langmuir-Hinshelwood, orde pertama semu Lagergren, dan orde kedua semu Ho-McKay. Penelitian ini menunjukkan bahwa pH optimum adsorpsi ion Ni(II) oleh hidroksiapatit dicapai pada pH 6,0. Adsorpsi ion Ni(II) oleh hidroksiapatit mengikuti model isotermal Langmuir dengan kapasitas adsorpsi sebesar 4,35 x 10-4 mol g-1. Selanjutnya, adsorpsi Ni(II) oleh hidroksiapatit dapat digambarkan melalui model kinetika orde kedua semu Ho-McKay dengan konstanta laju adsorpsi sebesar 477,68 g menit-1 mol-1.

Application of hydroxyapatite from the duck egg shell as adsorbent for Ni(II) ion had been conducted. The purposes of this research were to determine the optimum pH, the adsorption isotherm, the kinetic adsorption model of Ni(II) adsorption on the hydroxyapatite from the duck egg shell. The preparation of hydroxyapatite was conducted by dissolving the duck egg shell powder in 65% of HNO3 solution and followed by the addition of 85% of H3PO4 solution. The solution was adjusted to pH 10 using 37% of NH4OH solution. The suspension was maintained at room temperature for 24 h. The suspension was filtered, dried, and ground into a powder. The hydroxyapatite powder was heated at 600 degrees celsius for 3 h. The effect of pH on the adsorption of Ni(II) ion on the hydroxyapatite was carried out at different pH ranging from 2-7. The adsorption isotherm was evaluated using the Langmuir and Freundlich models at various initial concentration of adsorbate. Kinetic adsorption model was investigated using the Langmuir-Hinshelwood, the Lagergren pseudo first order, and the Ho-McKay pseudo second order models. The results showed that the optimum pH for ion Ni(II) adsorption on the hydroxyapatite was obtained at 6.0. The adsorption of Ni(II) ion on the hydroxyapatite followed the Langmuir isotherm model with the adsorption capacity of 4.35 x 10-4 mol g-1. In addition, the adsorption can be described by Ho-McKay pseudo second order with the adsorption rate constant of 477.68 g min-1 mol-1.

Kata Kunci : cangkang telur bebek, hidroksiapatit, ion nikel(II), isotermal adsorpsi, dan studi kinetika