Analisa Pengaruh Overheat Terhadap Perubahan Karakteristik Raw Material pada Proses Forging di PT Menara Terus Makmur

KURNIAWAN FAJAR S, Radhian Krisnaputra, S.T., M.Eng.

2018 | Tugas Akhir | D3 TEKNIK MESIN

Penempaan adalah proses pembentukan logam secara plastis menggunakan gaya tekan. Pada proses forging, material melalui proses heating, forging, dan trimming. Pada proses heating sering terjadi material yang mengalami overheat. Material SCM 440 yang dipanaskan di atas temperatur 1250 ⁰C dapat dikatakan material mengalami overheat. Material yang mengalami overheat dapat menyebabkan crack pada produk. Proses pengujian material SCM 440 yang dilakukan yaitu metalografi, kekerasan dan kekuatan tarik. Penelitian dilakukan dengan mengambil spesimen material SCM 440 dalam tiga kondisi, yaitu material no heating, return dan overheat. Spesimen tersebut sudah dipotong sesuai dengan ukuran pengujian. Hasil penelitian menunjukkan bahwa Struktur mikro pada material SCM 440 pada kondisi no heating, return, dan overheat tidak jauh berbeda, strukturnya masih berupa ferit dan perlit. Fasa perlit terlihat lebih dominan dibandingkan dengan fasa ferit. Pada material return fasa perlit lebih kasar dibanding dengan fasa perlit pada material no heating. Pada material overheat fasa perlit terlihat paling kasar dibanding dengan dua kondisi material lainnya. Kekerasan material SCM 440 pada kondisi overheat yaitu 298,367 HV, merupakan yang terendah dibandingkan dengan kondisi material yang lainnya. Material SCM 440 yang mengalami kondisi overheat menyebabkan fasa perlit terlihat lebih kasar. Hal tersebut mengakibatkan kekerasan material akan menurun. Selain itu, material yang mengalami overheat akan menjadi material yang getas diakibatkan oleh membesarnya grain size dan unsur paduan Mo, sehingga tidak dianjurkan untuk diproses forging.

Forging is the process of forming metal in a plastic manner using a compressive force. In the material forging process through the process of heating, forging, and trimming. In the heating process, the material often overheats. SCM440 material that heated at temperature above 1250 ⁰C can be said that the material has overheated. Materials that are overheated can cause cracks on the product. The testing process for SCM 440 material are metallography, hardness and tensile strength. The research was carried out by taking specimens of SCM 440 material in three conditions, there are material no heating, return and overheat. The specimen has been cut according to the size of the test. The results showed that the microstructure of SCM 440 material in no heating, return, and overheat conditions was not much different, the structure was still in the form of ferrite and pearlite. Pearlite phase looks more dominant compared to ferrite phase. The return material of pearlite phase is coarser than pearlite phase in no heating material. In pearlite phase overheat material looks more coarse compared to two other material condition. . The hardness of SCM 440 material in overheat condition is 298,367 HV, which is the lowest compared to other material conditions. SCM 440 material that is overheating causes phases of pearlite more rough. This causes material hardness to decrease. In addition, material that is overheated will become brittle material due to the enlargement of the grain size and Mo alloy material, so it is not recommended for forging process.

Kata Kunci : overheat, return, no heating.