PENGARUH AGEN PENSTABIL NATRIUM SITRAT DAN POLIETILEN GLIKOL PADA UKURAN NANOPARTIKEL Fe3O4

AQIDATUL IZZA, Drs. Roto, M.Eng., Ph.D. ; Dra. Eko Sri Kunarti, M.Si, Ph.D

2018 | Skripsi | S1 KIMIA

Nanomaterial magentik banyak diteliti karena kemungkinan aplikasi yang luas. Sintesis Fe3O4 dengan agen penstabil ion sitrat dan polietilen glikol (PEG) telah dilakukan. Penelitian ini bertujuan untuk mempelajari pengaruh agen penstabil natrium sitrat dan polietilen glikol terhadap bentuk dan ukuran nanopartikel magnetit, Fe3O4. Sintesis Fe3O4, Fe3O4/sitrat dan Fe3O4/PEG dilakukan dengan metode kopresipitasi pada pH terkontrol. Magnetit hasil sintesis dikarakterisasi dengan spektrofotometri infra merah, X-Ray Diffraction (XRD), Transmission Electron Microscopy (TEM) dan Scanning Electron Microscopy-Energy Dispersive X-Ray (SEM-EDX). Uji kualitatif kemagnetan juga dilakukan kepada ketiga material tersebut. Hasil penelitian menunjukkan bahwa agen penstabil dapat mempengaruhi proses nukleasi dan pertumbuhan kristal sehingga diperoleh partikel yang lebih bersifat monodispersi. Nanopartikel Fe3O4 yang disintesis dengan penstabil natrium sitrat memiliki diameter sekitar 12 nm dan penstabil PEG memiliki diameter sekitar 10 nm. Natrium sitrat membentuk koloid nanopartikel magnetit dengan mode stabilisasi elektrostatik sementara PEG dengan mode stabilisasi sterik.

Magnetic nanomaterials are intensively studied because of the possibility of various application. Synthesis of Fe3O4 with citrate ion and polyethylene glycol (PEG) as stabilizing agents was carried out. This study aims to study the effect of sodium citrate and polyethylene glycol as stabilizing agents on the shape and size of Fe3O4 magnetite nanoparticles. Synthesis of Fe3O4, Fe3O4/citrate, and Fe3O4/PEG was carried out by coprecipitation method at controlled pH. The products were characterized by infrared spectrophotometry, X-Ray Diffraction (XRD), Transmission Electron Microscopy (TEM) and Scanning Electron Microscopy-Energy Dispersive X-Ray (SEM-EDX). Qualitative tests of magnetism were also carried out on the three materials. The results showed that the stabilizing agent could influence the nucleation and crystal growth processes for obtaining more monodispersed particles. Fe3O4 nanoparticles prepared with sodium citrate and PEG have a diameter of 12 and 10 nm, respectively. Sodium citrate leads to Fe3O4 colloidal nanoparticle with electrostatic stabilization mode, whereas PEG leads to Fe3O4 colloidal nanoparticle with steric stabilization mode.

Kata Kunci : agen penstabil, Fe3O4, sitrat, polietilen glikol.