MODIFIKASI KARBON DOT TERKONJUGASI KOLISTIN UNTUK DETEKSI Escherichia coli: PENGARUH KONSENTRASI KOLISTIN SULFAT PADA INTENSITAS FLUORESENSI

NICKO AUDIO HARYANTO, Suherman, S.Si., M.Sc., Ph.D. ; Prof. Dr. Mudasir, M.Eng.

2018 | Skripsi | S1 KIMIA

Telah dilakukan modifikasi karbon dot terkonjugasi kolistin untuk deteksi Escherichia coli serta mempelajari pengaruh konsentrasi kolistin sulfat pada intensitas fluoresensi. Tujuan penelitian ini untuk melakukan sintesis karbon dot dari ammonium sitrat, mengetahui pengaruh konsentrasi kolistin dalam karbon dot dengan terkonjugasi kolistin terhadap intensitas spektra fluoresensinya dan mengetahui hubungan intensitas fluoresensi karbon dot konsentrasi kolistin berbeda dengan deteksi keberadaan bakteri Escherichia coli pada sampel air. Penelitian diawali dengan sintesis karbon dot dan karbon dot kolistin dengan variasi konsentrasi kolistin 1,0; 1,5; 2,0 dan 2,5 mmol. Prekursor dikarakterisasi dengan FT-IR. Morfologi karbon dot kolistin dilihat dengan SEM dan TEM. Larutan kabon dot dan karbon dot kolistin diukur dengan spektrofotometer UV-Vis dan diberi panjang gelombang eksitasi dari 310-450 nm dengan spektrofluorofotometer. Karbon dot kolistin digunakan untuk deteksi bakteri E. coli dalam sampel dan dianalisis dengan spektrofluorofotometer pada eksitasi panjang gelombang di mana puncak intensitas fluoresensi tertinggi terjadi. Hasil penelitian menunjukkan bahwa intensitas puncak tertinggi fluoresensi karbon dot kolistin dengan konsentrasi kolistin 2,5 mmol panjang gelombang eksitasi 360 nm. Untuk deteksi E. coli, semua karbon dot kolistin menghasilkan spektra fluoresensi yang hampir sama dengan hubungan semakin tinggi konsentrasi E. coli pada sampel, intensitas emisi fluoresensi karbon dot kolistin semakin naik.

Modification of colistin-conjugated carbon dots for detection of Escherichia coli and study of the effect of colistin sulphate concentration on fluoresence intensity has been conducted. The purpose of this research is to synthesize of carbon dots from ammonium citrate, to understand the effect of colistin concentration in colistin-conjugated carbon dots on fluorescence intensity and to study the correlation between fluorescence intensity of colistin-conjugated carbon dots with variation of colistin concentration and detection of E. coli bacteria in water samples. This research was started synthesizing carbon dots and carbon dots colistin with variations of colistin concentration of 1.0; 1.5; 2.0 and 2.5 mmol. All precursor were characterized by using FT-IR. Morphological pattern were analyzed with SEM and TEM. The spectra of carbon dots and carbon dots colistin solutions were measured with a UV-Vis spectrophotometer and was determined by giving excitation radiation at 310-450 nm using spectrofluorophotometer. Carbon dots colistin was used for bacterial detection in samples with variation in E. coli concentration which is analyzed by spectrofluorophotometer using excitation wavelength where the highest fluorescence intensity occurs. The results showed carbon dots colistin with colistin concentration of 2.5 mmol has the highest fluorescence intensity at excitation wavelength of 360 nm. For detection of E. coli, all carbon dots colistin produced the same fluorescence spectra, the higher E. coli concentration in the sample, the more intensity of carbon dots colistin emission is obtained.

Kata Kunci : Escherichia coli, karbon dot, kolistin, fluoresensi