PENGARUH DERAJAT KEASAMAN (pH) SALIVA ASAM TERHADAP KONSENTRASI PELEPASAN ION NIKEL (Ni) PADA ALOI STAINLESS STEEL 316L

KESAR ADI PAMUNGKAS, Prof. Dr. drg. Widowati Siswomihardjo, M.S.; Dr. drg. Siti Sunarintyas, M.Kes

2018 | Skripsi | S1 KEDOKTERAN GIGI

Pelepasan ion logam stainless steel dapat terjadi karena proses korosi yang disebabkan oleh pH yang rendah. Ion logam yang sering terlepas dari aloi stainless steel adalah ion Fe, Cr, Ni. Pelepasan ion nikel dapat menyebabkan reaksi alergi berupa stomatitis kontak dan reaksi hipersensitivitas. Tujuan dari penelitian ini adalah untuk mengetahui pengaruh derajat keasaman (pH) saliva asam terhadap konsentrasi pelepasan ion nikel (Ni) pada aloi stainless steel 316L. Subjek penelitian ini adalah 12 spesimen aloi stainless steel 316L dengan ukuran 10 mm x 10 mm x 1 mm. Subjek penelitian dibagi menjadi 3 kelompok yaitu, kelompok A, B, dan C yang direndam dalam larutan saliva buatan pH 3, 5, dan 7. Perendaman spesimen dilakukan di dalam botol polietilen yang berisi larutan saliva buatan sebanyak 20 ml untuk masing-masing botol selama 14 hari pada suhu 37oC. Pada hari ke 15 spesimen diambil dari botol politetilen dan dilakukan pengukuran konsentrasi ion nikel yang terlepas dari sampel dengan menggunakan alat spektrofotometri serapan atom (SSA) dengan satuan parts per million (ppm). Analisis data dilakukan menggunakan uji ANAVA satu-jalur. Hasil penelitian menunjukkan nilai rerata konsentrasi pelepasan ion nikel pada aloi stainless steel 316L untuk kelompok pH 3, 5, dan 7 secara berurutan adalah (0,099±0,023)ppm, (0,045±0,020)ppm, dan (0,000±0,000)ppm. Hasil uji anava satu-jalur menunjukkan bahwa derajat keasaman (pH) saliva asam berpengaruh signifikan terhadap konsentrasi pelepasan ion nikel (Ni) antar kelompok perlakuan (p<0,05). Kesimpulan penelitian ini adalah semakin rendah derajat keasaman (pH) saliva maka semakin tinggi konsentrasi pelepasan ion nikel (Ni) pada aloi stainless steel 316L.

The release of stainless steel metal ions can occur due to corrosion processes caused by low pH. Metal ions often released from stainless steel alloys are Fe, Cr, Ni. The release of nickel ions can cause allergic reactions in the form of contact stomatitis and hypersensitivity reactions. The purpose of this study was to determine the influence of acid acidity (pH) of saliva on the concentration of nickel (Ni) ions release of 316L stainless steel alloy. The subjects of this study were 12 specimens of 316L stainless steel alloy with size 10 mm x 10 mm x 1 mm. The subjects were divided into 3 groups, group A, B, and C immersed in artificial saliva solution of pH 3, 5, and 7. The immersion of the specimen was carried out in a polyethylene bottle containing 20 ml artificial saliva solution for each bottle for 14 days at 37°C. On the 15th day, the specimen was taken from the polyethylene bottle and measured the concentration of nickel ions released from the sample using an atomic absorption spectrophotometry (AAS) device in parts per million (ppm). Data analysis was performed using one-way ANOVA test. The result showed that the mean of concentration value of nickel (Ni) ion released by 316L stainless steel alloy for group pH of 3, 5, and 7 were (0.099±0.023)ppm, (0.045±0.020)ppm, dan (0.000±0.000)ppm. One-way ANOVA test result showed that acid acidity (pH) of saliva significantly influenced nickel (Ni) ions concentration between treatment groups (p<0.05). The conclusion of this research is that the lower acidity (pH) of saliva, the higher concentration of nickel (Ni) ions release of 316L stainless steel alloy.

Kata Kunci : Kata Kunci : Stainless steel 316L, pelepasan ion, nikel, pH / Keywords : 316L stainless steel, ion release, nickel, pH