RENDEMEN DAN SIFAT FISIK PULP SULFAT KAYU MERANTI MERAH (Shorea selanica BI.)

ERLIANA CHANDRA RUKMI, Prof. Dr. Ir. Sri Nugroho Marsoem, M.Agr.Sc ;Dr. Joko Sulistyo, S.Hut., M.Sc

2018 | Skripsi | S1 KEHUTANAN

Kayu meranti merah (Shorea selanica BI.) merupakan kayu yang mulai dipertimbangkan ditanam di hutan tanaman dengan konsep silvikultur intensif. Dimensi serat dan berat jenis kayu meranti merah memperlihatkan kesesuaiannya sebagai bahan baku untuk pembuatan pulp dan kertas, oleh karena itu kayu meranti merah telah diteliti untuk diolah menjadi pulp melalui proses sulfat. Penelitian dilakukan dengan menggunakan rancangan acak lengkap yang menggunakan dua faktor, yaitu konsentrasi sulfiditas dan waktu pemasakan. Awal mula batang kayu meranti merah ditebang lalu dibentuk disk dengan ketebalan 3 cm dan diceriping dengan ukuran 3x3x0,3 cm. Ceriping tersebut dimasak dengan menggunakan proses sulfat dengan tiga konsentrasi sulfiditas yang digunakan yaitu, 20%, 22%, dan 24% dan waktu pemasakan yang digunakan adalah 2 jam dan 2,5 jam. Masing-masing dilakukan 3 kali pengulangan dengan total 18 sampel. Hasil penelitian menunjukan kayu meranti merah dapat diolah menjadi pulp dengan rendemen tersaring yaitu berkisar antara 35,14% sampai 48,58% dan sifat fisiknya yaitu indeks jebol berkisar antara 1,77 sampai 4,22 kPa.m2/g, indeks tarik 12,50 sampai 41,80 Nm/g, serta indeks sobek 1,77 sampai 4,32 mN.m2/g. Analisis varian menunjukan bahwa pengaruh antara konsentrasi sulfiditas dan waktu pemasakan tidak menunjukan interaksi terhadap seluruh parameter. Konsentrasi sulfiditas tidak berpengaruh nyata terhadap rendemen tersaring dan indeks tarik, namun berpengaruh nyata terhadap indeks jebol dan berpengaruh sangat nyata terhadap indeks sobek. Waktu pemasakan berpengaruh nyata terhadap rendemen tersaring dan indeks sobek, namun tidak berpengaruh nyata terhadap indeks jebol dan indeks tarik.

Red meranti wood (Shorea selanica BI.) has recently been introduced as one of species use in an Intensive Silviculture concept. Initial study on the fibre dimension and wood density showed that this wood is suitable as the raw material for pulp and paper making. Therefore, a study on the pulping of red meranti wood had been conducted by using kraft process. The obtained data was analysed by using completely randomized design of two factors, that is sulfidity concentration and cooking time. The trunk of red meranti wood was cut then was formed into discs with thickness 3 cm and chipped with size of 3x3x0,3 cm. The chip was processed by kraft process with sulfidity were of, 20%, 22%, 24% while cooking time were 2 and 2.5 hours. Each of 3 replication with total 18 samples. The result showed that red meranti wood could be processed into pulp with a yield of 35.14% to 48.58%. The physical properties of the pulp were 1.77 to 4.22 kPa.m2/g, 12.50 to 41.80 Nm/g, and 1.77 to 4.32 mN.m2/g for bursting, tensile, and tearing strength respectively. Analysis of varians on the data obtained revealed that there was no interaction effect between sulfidity and cooking time for all the parameters observed. There were no significant effect of the sulfidity on the pulp yield and tensile strength, but the effect was significant on the burst strength and very significant on the tearing strength. Cooking time caused significant effect on the pulp yield and tensile strength, but did not give significant effect on the bursting and tearing strength.

Kata Kunci : Shorea selanica, Physical Properties, Yield, Cooking Time;Shorea selanica, Sifat Pulp Sulfat, Rendemen, Waktu Pemasakan